Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.67 g/cm³ Show Material materials with Density of 2.67 g/cm³ | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | |
2.67 g/cm³ Show Material materials with Density of 2.67 g/cm³ | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | ||
20.0 °C | 2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ | H12 | EN 573-3 | Flat |
Dimension
| Property | Value | Condition | Related Standards | Thickness | Shape |
|---|---|---|---|---|---|
Thickness | 0.2 mm Show Material materials with Thickness of 0.2 mm | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | 0.2 mm | Coil, Sheet, Strip |
6.0 mm Show Material materials with Thickness of 6.0 mm | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | 6.0 mm | Coil, Sheet, Strip |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 125.0 MPa Show Material materials with Bending Fatigue Strength of 125.0 MPa | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | ||
Elastic modulus | 68.6 GPa Show Material materials with Elastic modulus of 68.6 GPa | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | ||
70.5 GPa Show Material materials with Elastic modulus of 70.5 GPa | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | |||
20.0 °C | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H12 | EN 573-3 | Flat | ||
Elongation | 3.0 - 6.0 % Show Material materials with Elongation of 3.0 - 6.0 % | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | A50 | |
3.0 % Show Material materials with Elongation of 3.0 % | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | A50 | ||
4.0 % Show Material materials with Elongation of 4.0 % | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | A50 | ||
5.0 % Show Material materials with Elongation of 5.0 % | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | A50 | ||
6.0 % Show Material materials with Elongation of 6.0 % | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | A50 | ||
6.0 % Show Material materials with Elongation of 6.0 % | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | A100 | ||
7.0 % Show Material materials with Elongation of 7.0 % | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | A50 | ||
20.0 °C | 3.0 % Show Material materials with Elongation of 3.0 % | H12 | EN 573-3 | Flat | A50 Transverse | |
20.0 °C | 3.0 % Show Material materials with Elongation of 3.0 % | H12 | EN 573-3 | Flat | A50 | |
20.0 °C | 4.0 % Show Material materials with Elongation of 4.0 % | H12 | EN 573-3 | Flat | A50 Transverse | |
20.0 °C | 4.0 % Show Material materials with Elongation of 4.0 % | H12 | EN 573-3 | Flat | A50 | |
20.0 °C | 5.0 % Show Material materials with Elongation of 5.0 % | H12 | EN 573-3 | Flat | A50 Transverse | |
20.0 °C | 5.0 % Show Material materials with Elongation of 5.0 % | H12 | EN 573-3 | Flat | A50 | |
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | H12 | EN 573-3 | Flat | A50 Transverse | |
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | H12 | EN 573-3 | Flat | Transverse | |
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | H12 | EN 573-3 | Flat | A50 | |
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | H12 | EN 573-3 | Flat | ||
20.0 °C | 7.0 % Show Material materials with Elongation of 7.0 % | H12 | EN 573-3 | Flat | A50 Transverse | |
20.0 °C | 7.0 % Show Material materials with Elongation of 7.0 % | H12 | EN 573-3 | Flat | A50 | |
Hardness, Brinell | 75.0 [-] Show Material materials with Hardness, Brinell of 75.0 [-] | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | ||
20.0 °C | 75.0 [-] Show Material materials with Hardness, Brinell of 75.0 [-] | H12 | EN 573-3 | Flat | ||
Hardness, HBW | 75 [-] Show Material materials with Hardness, HBW of 75 [-] | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 20.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | H12 | EN 573-3 | Flat | |
Shear modulus | 25.725 GPa Show Material materials with Shear modulus of 25.725 GPa | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | ||
26.6 GPa Show Material materials with Shear modulus of 26.6 GPa | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | |||
20.0 °C | 26.6 GPa Show Material materials with Shear modulus of 26.6 GPa | H12 | EN 573-3 | Flat | ||
Tensile strength | 20.0 °C | 250.0 - 305.0 MPa Show Material materials with Tensile strength of 250.0 - 305.0 MPa | H12 | EN 573-3 | Flat | Transverse |
20.0 °C | 250.0 - 305.0 MPa Show Material materials with Tensile strength of 250.0 - 305.0 MPa | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2, EN 573-3, EN 485 | Coil, Sheet, Strip, Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire, Flat | ||
Yield strength | 190.0 MPa Show Material materials with Yield strength of 190.0 MPa | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | RP02 | |
190 MPa Show Material materials with Yield strength of 190 MPa | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | |||
20.0 °C | 190.0 MPa Show Material materials with Yield strength of 190.0 MPa | H12 | EN 573-3 | Flat | RP02 Transverse | |
20.0 °C | 190.0 MPa Show Material materials with Yield strength of 190.0 MPa | H12 | EN 573-3 | Flat | RP02 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 100 °C | 0.000024 1/K Show Material materials with Coefficient of thermal expansion of 0.000024 1/K | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | 20-100°C |
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Melting point | 560.0 - 655.0 °C Show Material materials with Melting point of 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Specific heat capacity | 20.0 °C | 897.0 J/(kg·K) Show Material materials with Specific heat capacity of 897.0 J/(kg·K) | H12 | EN 573-3 | Flat | |
Thermal conductivity | 134 W/(m·K) Show Material materials with Thermal conductivity of 134 W/(m·K) | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | ||
20.0 °C | 129.0 W/(m·K) Show Material materials with Thermal conductivity of 129.0 W/(m·K) | H12 | EN 573-3 | Flat |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium | ||||
Electrical resistivity | 5.2e-08 Ω·m Show Material materials with Electrical resistivity of 5.2e-08 Ω·m | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | ||
20.0 °C | 5.4e-08 Ω·m Show Material materials with Electrical resistivity of 5.4e-08 Ω·m | H12 | EN 573-3 | Flat |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.25 % Show Material materials with Chromium of 0.25 % | H12 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
0.25 % Show Material materials with Chromium of 0.25 % | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H12 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
0.1 % Show Material materials with Copper of 0.1 % | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | |
Iron | 0.5 % Show Material materials with Iron of 0.5 % | H12 | EN 573-3 | Flat |
0.5 % Show Material materials with Iron of 0.5 % | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | |
0.50 % Show Material materials with Iron of 0.50 % | H12 | EN 573-3, EN 485 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | |
Magnesium | 3.1 - 3.9 % Show Material materials with Magnesium of 3.1 - 3.9 % | H12 | EN 573-3, EN 573-1, EN 573-2, EN 573-3, EN 485-2, EN 485 | Flat, Coil, Sheet, Strip, Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Manganese | 0.5 % Show Material materials with Manganese of 0.5 % | H12 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
0.5 % Show Material materials with Manganese of 0.5 % | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | |
Other | 0.05 - 0.15 % Show Material materials with Other of 0.05 - 0.15 % | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip |
Silicon | 0.5 % Show Material materials with Silicon of 0.5 % | H12 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
0.5 % Show Material materials with Silicon of 0.5 % | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | |
Titanium | 0.2 % Show Material materials with Titanium of 0.2 % | H12 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
0.2 % Show Material materials with Titanium of 0.2 % | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip | |
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % | H12 | EN 573-3, EN 485 | Flat, Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
0.2 % Show Material materials with Zinc of 0.2 % | H12 | EN 573-1, EN 573-2, EN 573-3, EN 485-2 | Coil, Sheet, Strip |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Excellent | |
| Application areas | Furniture, Plinths, Blinds: Single sheet, Intermediate transformation/interior use; Food can: Body, Lids | |
| Brazing | hard brazing (with flux/ without flux): sufficient - not suitable / sufficient, friction soldering: acceptable, soft brazing with flux: poor | |
| Corrosion properties | Excellent | |
| General machinability | Good | |
| Welding | Good | |
| Workability | Good | |