EN 573-3 Grade AW-5154A H18

Want to keep this datasheet? Save it now in your required format

Description

Material EN AW-Al Mg3,5(B) is produced for sheet metal, strip and plates, wire and prewire for mechanical and welding applications, for extruded and drawn components. The alloy is food-safe.

Related Standards

Equivalent Materials

This material data has been provided by WIAM,Aludium,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperature

Density

2.68 g/cm³

Show Material materials with Density of 2.68 g/cm³ at 20.0 °C

20.0 °C

2.67 g/cm³

Show Material materials with Density of 2.67 g/cm³ at 23.0 °C

23.0 °C

Dimension

PropertyValue

Thickness

0.2 - 3 mm

Show Material materials with Thickness of 0.2 - 3 mm

Mechanical

PropertyValueTemperatureComment

Bending Fatigue Strength

145 MPa

Show Material materials with Bending Fatigue Strength of 145 MPa at 23.0 °C

23.0 °C

Elastic modulus

70 GPa

Show Material materials with Elastic modulus of 70 GPa at 20.0 °C

20.0 °C

68.6 - 70.5 GPa

Show Material materials with Elastic modulus of 68.6 - 70.5 GPa at 23.0 °C

23.0 °C

Unlock all property charts

Elongation

3 %

Show Material materials with Elongation of 3 % at 20.0 °C

20.0 °C

2 %

Show Material materials with Elongation of 2 % at 23.0 °C

23.0 °C

Unlock all property charts

Elongation A100

2 %

Show Material materials with Elongation A100 of 2 % at 20.0 °C

20.0 °C

3 %

Show Material materials with Elongation A100 of 3 % at 23.0 °C

23.0 °C

Unlock all property charts

Elongation A50

1 - 2 %

Show Material materials with Elongation A50 of 1 - 2 % at 20.0 °C

20.0 °C

1 - 2 %

Show Material materials with Elongation A50 of 1 - 2 % at 23.0 °C

23.0 °C

Unlock all property charts

Elongation A50, transverse

1 %

Show Material materials with Elongation A50, transverse of 1 % at 20.0 °C

20.0 °C

Hardness, Brinell

80 - 94 [-]

Show Material materials with Hardness, Brinell of 80 - 94 [-] at 20.0 °C

20.0 °C

100 [-]

Show Material materials with Hardness, Brinell of 100 [-] at 23.0 °C

23.0 °C

Unlock all property charts

Hardness, HBW

94 [-]

Show Material materials with Hardness, HBW of 94 [-] at 23.0 °C

23.0 °C

Plane-Strain Fracture Toughnes

22 - 35 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-] at 20.0 °C

20.0 °C

Shear modulus

26.6 GPa

Show Material materials with Shear modulus of 26.6 GPa at 20.0 °C

20.0 °C

25.73 - 26.6 GPa

Show Material materials with Shear modulus of 25.73 - 26.6 GPa at 23.0 °C

23.0 °C

Unlock all property charts

Tensile strength

310 - 330 MPa

Show Material materials with Tensile strength of 310 - 330 MPa at 20.0 °C

20.0 °C

310 - 330 MPa

Show Material materials with Tensile strength of 310 - 330 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Tensile strength, transverse

310 MPa

Show Material materials with Tensile strength, transverse of 310 MPa at 20.0 °C

20.0 °C

Yield strength

270 MPa

Show Material materials with Yield strength of 270 MPa at 23.0 °C

23.0 °C

Yield strength Rp0.2

240 - 320 MPa

Show Material materials with Yield strength Rp0.2 of 240 - 320 MPa at 20.0 °C

20.0 °C

240 - 320 MPa

Show Material materials with Yield strength Rp0.2 of 240 - 320 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Yield strength Rp0.2, transverse

270 MPa

Show Material materials with Yield strength Rp0.2, transverse of 270 MPa at 20.0 °C

20.0 °C

Thermal

PropertyValueTemperatureComment

Coefficient of thermal expansion

2.4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.4E-5 1/K at 100.0 °C

100.0 °C

20-100°C

Max service temperature

150 °C

Show Material materials with Max service temperature of 150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

560 - 655 °C

Show Material materials with Melting point of 560 - 655 °C

Typical for Wrought 5000 Series Aluminium

Specific heat capacity

897 J/(kg·K)

Show Material materials with Specific heat capacity of 897 J/(kg·K) at 20.0 °C

20.0 °C

Thermal conductivity

129 W/(m·K)

Show Material materials with Thermal conductivity of 129 W/(m·K) at 20.0 °C

20.0 °C

134 W/(m·K)

Show Material materials with Thermal conductivity of 134 W/(m·K) at 23.0 °C

23.0 °C

Unlock all property charts

Electrical

PropertyValueTemperatureComment

Electrical conductivity

1.80E+7 - 3.10E+7 S/m

Show Material materials with Electrical conductivity of 1.80E+7 - 3.10E+7 S/m at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Electrical resistivity

5.4E-8 Ω·m

Show Material materials with Electrical resistivity of 5.4E-8 Ω·m at 20.0 °C

20.0 °C

5.2E-8 Ω·m

Show Material materials with Electrical resistivity of 5.2E-8 Ω·m at 23.0 °C

23.0 °C

Unlock all property charts

Chemical properties

Property

Chromium

0.25 %

Copper

0.1 %

Iron

0.5 %

Magnesium

3.1 - 3.9 %

Manganese

0.5 %

Other

0.05 - 0.15 %

Mn + Cr = 0.1 - 0.5, Be < 0.0003 for welding additives, each 0.05, total 0.15, Rest Al

Silicon

0.5 %

Titanium

0.2 %

Zinc

0.2 %

Technological properties

Property
Anodizing

Excellent

Application areas

Furniture, Plinths, Blinds: Single sheet, Intermediate transformation/interior use; Food can: Body, Lids

Brazing

hard brazing (with flux/ without flux): sufficient - not suitable / sufficient, friction soldering: acceptable, soft brazing with flux: poor

Corrosion properties

Excellent

General machinability

Good

Welding

Good

Workability

Good