Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.67 g/cm³ Show Material materials with Density of 2.67 g/cm³ | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.5 GPa Show Material materials with Elastic modulus of 70.5 GPa | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 26.6 GPa Show Material materials with Shear modulus of 26.6 GPa | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | |
Tensile strength | 210.0 - 250.0 MPa Show Material materials with Tensile strength of 210.0 - 250.0 MPa | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C Show Material materials with Melting point of 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) Show Material materials with Thermal conductivity of 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.25 % Show Material materials with Chromium of 0.25 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Magnesium | 3.1 - 3.9 % Show Material materials with Magnesium of 3.1 - 3.9 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Manganese | 0.5 % Show Material materials with Manganese of 0.5 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Silicon | 0.5 % Show Material materials with Silicon of 0.5 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Titanium | 0.2 % Show Material materials with Titanium of 0.2 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): sufficient - not suitable / sufficient, friction soldering: acceptable, soft brazing with flux: poor | |
| Corrosion properties | Seawater: very good to good, weathering: very good | |
| Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (O) | |