Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ | T6 | AA Standards, ASTM B247 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 110.0 MPa Show Material materials with Bending Fatigue Strength of 110.0 MPa | T6 | AA Standards | |
Elastic modulus | 79.0 GPa Show Material materials with Elastic modulus of 79.0 GPa | T6 | AA Standards, ASTM B247 | |
Hardness, Brinell | 120.0 [-] Show Material materials with Hardness, Brinell of 120.0 [-] | T6 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 4000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 4000 Series Aluminium | ||
Shear modulus | 26.0 GPa Show Material materials with Shear modulus of 26.0 GPa | Typical for Wrought 4000 Series Aluminium | ||
Tensile strength | 360.0 MPa Show Material materials with Tensile strength of 360.0 MPa | T6 | AA Standards, ASTM B247 | |
380.0 MPa Show Material materials with Tensile strength of 380.0 MPa | T6 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 1.9399999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.9399999999999997e-05 1/K | T6 | AA Standards, ASTM B247 | |
100 °C | 1.9399999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.9399999999999997e-05 1/K | T6 | AA Standards, ASTM B247 | ||
Melting point | 530.0 - 570.0 °C Show Material materials with Melting point of 530.0 - 570.0 °C | T6 | AA Standards, ASTM B247 | ||
Specific heat capacity | 864.0 J/(kg·K) Show Material materials with Specific heat capacity of 864.0 J/(kg·K) | Typical for Wrought 4000 Series Aluminium | |||
Thermal conductivity | 138.0 - 155.0 W/(m·K) Show Material materials with Thermal conductivity of 138.0 - 155.0 W/(m·K) | T6 | AA Standards, ASTM B247 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 20000000.0 - 23000000.0 S/m Show Material materials with Electrical conductivity of 20000000.0 - 23000000.0 S/m | T6 | AA Standards, ASTM B247 |
Electrical resistivity | 4.35e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 4.35e-08 - 5e-08 Ω·m | T6 | AA Standards, ASTM B247 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T6 | AA Standards, ASTM B247 |
Copper | 0.5 - 1.3 % Show Material materials with Copper of 0.5 - 1.3 % | T6 | AA Standards, ASTM B247 |
Iron | 1.00 % Show Material materials with Iron of 1.00 % | T6 | AA Standards, ASTM B247 |
Magnesium | 0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 % | T6 | AA Standards, ASTM B247 |
Nickel | 0.5 - 1.3 % Show Material materials with Nickel of 0.5 - 1.3 % | T6 | AA Standards, ASTM B247 |
Silicon | 11.0 - 13.5 % Show Material materials with Silicon of 11.0 - 13.5 % | T6 | AA Standards, ASTM B247 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T6 | AA Standards, ASTM B247 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation, limited damage during laboratory tests, general: acceptable, in principle it should be protected | |
| General machinability | General: good to acceptable | |
| Workability | Moderate Workability | |