General
Property | Value | Temperature |
---|---|---|
Density | 2.68 - 2.69 g/cm³ Show Material materials with Density of 2.68 - 2.69 g/cm³ at 20.0 °C | 20.0 °C |
2.68 - 2.69 g/cm³ Show Material materials with Density of 2.68 - 2.69 g/cm³ at 23.0 °C | 23.0 °C | |
Dimension
Property | Value |
---|---|
Thickness | 0.2 - 4 mm Show Material materials with Thickness of 0.2 - 4 mm |
Mechanical
Property | Value | Temperature | Comment |
---|---|---|---|
Bending angle 180° | 3 °/t Show Material materials with Bending angle 180° of 3 °/t at 23.0 °C | 23.0 °C | |
Bending angle 90° | 1 - 3 °/t Show Material materials with Bending angle 90° of 1 - 3 °/t at 23.0 °C | 23.0 °C | |
Elastic modulus | 70 GPa Show Material materials with Elastic modulus of 70 GPa at 20.0 °C | 20.0 °C | |
68.6 - 70 GPa Show Material materials with Elastic modulus of 68.6 - 70 GPa at 23.0 °C | 23.0 °C | ||
Elongation | 3 % Show Material materials with Elongation of 3 % at 20.0 °C | 20.0 °C | |
Elongation A100 | 3 - 5 % Show Material materials with Elongation A100 of 3 - 5 % at 23.0 °C | 23.0 °C | |
Elongation A50 | 2 - 7 % Show Material materials with Elongation A50 of 2 - 7 % at 20.0 °C | 20.0 °C | |
2 - 7 % Show Material materials with Elongation A50 of 2 - 7 % at 23.0 °C | 23.0 °C | ||
Elongation A50, transverse | 3 - 7 % Show Material materials with Elongation A50, transverse of 3 - 7 % at 20.0 °C | 20.0 °C | |
Hardness, Brinell | 69 - 70 [-] Show Material materials with Hardness, Brinell of 69 - 70 [-] at 20.0 °C | 20.0 °C | |
69 [-] Show Material materials with Hardness, Brinell of 69 [-] at 23.0 °C | 23.0 °C | ||
Hardness, HBW | 69 [-] Show Material materials with Hardness, HBW of 69 [-] at 23.0 °C | 23.0 °C | |
Plane-Strain Fracture Toughnes | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C | 23.0 °C | Typical for Wrought 5000 Series Aluminium |
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] at 20.0 °C | 20.0 °C | |
Shear modulus | 26.3 - 26.5 GPa Show Material materials with Shear modulus of 26.3 - 26.5 GPa at 20.0 °C | 20.0 °C | |
26.3 GPa Show Material materials with Shear modulus of 26.3 GPa at 23.0 °C | 23.0 °C | ||
Tensile strength | 220 - 270 MPa Show Material materials with Tensile strength of 220 - 270 MPa at 20.0 °C | 20.0 °C | |
220 - 270 MPa Show Material materials with Tensile strength of 220 - 270 MPa at 23.0 °C | 23.0 °C | ||
Tensile strength, transverse | 230 - 270 MPa Show Material materials with Tensile strength, transverse of 230 - 270 MPa at 20.0 °C | 20.0 °C | |
Yield strength | 170 MPa Show Material materials with Yield strength of 170 MPa at 23.0 °C | 23.0 °C | |
Yield strength Rp0.2 | 170 - 180 MPa Show Material materials with Yield strength Rp0.2 of 170 - 180 MPa at 20.0 °C | 20.0 °C | |
170 - 210 MPa Show Material materials with Yield strength Rp0.2 of 170 - 210 MPa at 23.0 °C | 23.0 °C | ||
Yield strength Rp0.2, transverse | 170 MPa Show Material materials with Yield strength Rp0.2, transverse of 170 MPa at 20.0 °C | 20.0 °C |
Thermal
Property | Value | Temperature | Comment |
---|---|---|---|
Coefficient of thermal expansion | 2.37E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.37E-5 1/K at 20.0 °C | 20.0 °C | 20-100°C |
2.37E-5 - 2.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.37E-5 - 2.4E-5 1/K at 100.0 °C | 100.0 °C | 20-100°C | |
Max service temperature | 150 °C Show Material materials with Max service temperature of 150 °C | Typical for Wrought 5000 Series Aluminium | |
Melting point | 610 - 650 °C Show Material materials with Melting point of 610 - 650 °C | ||
Specific heat capacity | 898 - 921 J/(kg·K) Show Material materials with Specific heat capacity of 898 - 921 J/(kg·K) at 20.0 °C | 20.0 °C | |
Thermal conductivity | 149 - 167 W/(m·K) Show Material materials with Thermal conductivity of 149 - 167 W/(m·K) at 20.0 °C | 20.0 °C | |
140 - 160 W/(m·K) Show Material materials with Thermal conductivity of 140 - 160 W/(m·K) at 23.0 °C | 23.0 °C | ||
Electrical
Property | Value | Temperature |
---|---|---|
Electrical conductivity | 2.60E+7 S/m Show Material materials with Electrical conductivity of 2.60E+7 S/m at 20.0 °C | 20.0 °C |
2.50E+7 - 3.00E+7 S/m Show Material materials with Electrical conductivity of 2.50E+7 - 3.00E+7 S/m at 23.0 °C | 23.0 °C | |
Electrical resistivity | 4.6E-8 Ω·m Show Material materials with Electrical resistivity of 4.6E-8 Ω·m at 20.0 °C | 20.0 °C |
3.33E-8 - 4.5E-8 Ω·m Show Material materials with Electrical resistivity of 3.33E-8 - 4.5E-8 Ω·m at 23.0 °C | 23.0 °C | |
Chemical properties
Property | ||
---|---|---|
Chromium | 0.15 % | |
Copper | 0.15 % | |
Iron | 0.5 % | |
Magnesium | 1.7 - 2.4 % | |
Manganese | 0.1 - 0.5 % | |
Other | 0.05 - 0.15 % | each 0.05, total 0.15, Rest Al |
Silicon | 0.4 % | |
Titanium | 0.15 % | |
Zinc | 0.15 % |
Technological properties
Property | ||
---|---|---|
Anodizing | Excellent | |
Application areas | Facades: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Tubes: Industrial tubes, Pipes; Wind energy: Nacelle coverings, rotor hub, stairs; | |
Brazing | hard brazing (with flux/ without flux): sufficient / poor, friction soldering: good, soft brazing with flux: sufficient | |
Corrosion properties | Excellent | |
Welding | Very Good | |
Workability | Very Good |