Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.66 g/cm³ Show Material materials with Density of 2.66 g/cm³ | H34 | AA Standards, ASTM B209 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 130.0 MPa Show Material materials with Bending Fatigue Strength of 130.0 MPa | H34 | AA Standards | ||
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H34 | AA Standards, ASTM B209 | ||
Elongation A100 | 23.0 °C | 9 % Show Material materials with Elongation A100 of 9 % | |||
Elongation A50 | 23.0 °C | 4 - 13 % Show Material materials with Elongation A50 of 4 - 13 % | |||
Hardness, Brinell | 73.0 [-] Show Material materials with Hardness, Brinell of 73.0 [-] | H34 | AA Standards | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | |||
Tensile strength | 290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | H34 | AA Standards | ||
270.0 - 320.0 MPa Show Material materials with Tensile strength of 270.0 - 320.0 MPa | H34 | AA Standards, ASTM B209 | |||
Yield strength Rp0.2 | 23.0 °C | 200 - 230 MPa Show Material materials with Yield strength Rp0.2 of 200 - 230 MPa | |||
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 100 °C, 20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | H34 | AA Standards, ASTM B209 | |
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 590.0 - 645.0 °C Show Material materials with Melting point of 590.0 - 645.0 °C | H34 | AA Standards, ASTM B209 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 126 W/(m·K) Show Material materials with Thermal conductivity of 126 W/(m·K) | H34 | AA Standards, ASTM B209 | ||
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 19000000.0 S/m Show Material materials with Electrical conductivity of 19000000.0 S/m | H34 | AA Standards, ASTM B209 |
Electrical resistivity | 5.26e-08 Ω·m Show Material materials with Electrical resistivity of 5.26e-08 Ω·m | H34 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards | ||
|---|---|---|---|---|---|
Chromium | 0.15 - 0.35 % Show Material materials with Chromium of 0.15 - 0.35 % | H34 | AA Standards, ASTM B209 | ||
Copper | 0.05 % Show Material materials with Copper of 0.05 % | H34 | AA Standards, ASTM B209 | ||
Magnesium | 3.1 - 3.9 % Show Material materials with Magnesium of 3.1 - 3.9 % | H34 | AA Standards, ASTM B209 | ||
Manganese | 0.01 % Show Material materials with Manganese of 0.01 % | H34 | AA Standards, ASTM B209 | ||
Other | each 0.05, total 0.15, Rest Al, Si + Fe < 0.45 | ||||
Titanium | 0.05 % Show Material materials with Titanium of 0.05 % | H34 | AA Standards, ASTM B209 | ||
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % | H34 | AA Standards, ASTM B209 | ||
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |