Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2.66 g/cm³ Show Material materials with Density of 2.66 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Bending angle 180° | 23.0 °C | 2 - 3 °/t Show Material materials with Bending angle 180° of 2 - 3 °/t | |
Bending angle 90° | 23.0 °C | 0.5 - 3.5 °/t Show Material materials with Bending angle 90° of 0.5 - 3.5 °/t | |
Elastic modulus | 23.0 °C | 69 - 70 GPa Show Material materials with Elastic modulus of 69 - 70 GPa | Typical for Wrought 5000 Series Aluminium |
Elongation | 20.0 °C | 9 % Show Material materials with Elongation of 9 % | |
Elongation A100 | 23.0 °C | 9 % Show Material materials with Elongation A100 of 9 % | |
Elongation A50 | 20.0 °C | 5 - 10 % Show Material materials with Elongation A50 of 5 - 10 % | |
23.0 °C | 5 - 10 % Show Material materials with Elongation A50 of 5 - 10 % | ||
Elongation A50, transverse | 20.0 °C | 5 - 10 % Show Material materials with Elongation A50, transverse of 5 - 10 % | |
Elongation, transverse | 20.0 °C | 9 % Show Material materials with Elongation, transverse of 9 % | |
Hardness, Brinell | 20.0 °C | 90 [-] Show Material materials with Hardness, Brinell of 90 [-] | |
23.0 °C | 90 [-] Show Material materials with Hardness, Brinell of 90 [-] | ||
Plane-Strain Fracture Toughnes | 23.0 °C | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m | Typical for Wrought 5000 Series Aluminium |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium |
Shear modulus | 23.0 °C | 26 - 26.5 GPa Show Material materials with Shear modulus of 26 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium |
Shear strength | 20.0 °C | 90 MPa Show Material materials with Shear strength of 90 MPa | |
Tensile strength | 20.0 °C | 305 - 380 MPa Show Material materials with Tensile strength of 305 - 380 MPa | |
23.0 °C | 305 - 380 MPa Show Material materials with Tensile strength of 305 - 380 MPa | ||
Tensile strength, transverse | 20.0 °C | 305 - 380 MPa Show Material materials with Tensile strength, transverse of 305 - 380 MPa | |
Yield strength Rp0.2 | 20.0 °C | 220 MPa Show Material materials with Yield strength Rp0.2 of 220 MPa | |
23.0 °C | 220 MPa Show Material materials with Yield strength Rp0.2 of 220 MPa | ||
Yield strength Rp0.2, transverse | 20.0 °C | 220 MPa Show Material materials with Yield strength Rp0.2, transverse of 220 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.2E-5 - 2.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.2E-5 - 2.5E-5 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150 °C Show Material materials with Max service temperature of 150 °C | Typical for Wrought 5000 Series Aluminium | |
Melting point | 560 - 655 °C Show Material materials with Melting point of 560 - 655 °C | Typical for Wrought 5000 Series Aluminium | |
Specific heat capacity | 23.0 °C | 879 - 963 J/(kg·K) Show Material materials with Specific heat capacity of 879 - 963 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 23.0 °C | 112 - 205 W/(m·K) Show Material materials with Thermal conductivity of 112 - 205 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical conductivity | 23.0 °C | 1.80E+7 - 3.10E+7 S/m Show Material materials with Electrical conductivity of 1.80E+7 - 3.10E+7 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 23.0 °C | 3.3E-8 - 5E-8 Ω·m Show Material materials with Electrical resistivity of 3.3E-8 - 5E-8 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value |
|---|---|
Chromium | 0.25 % Show Material materials with Chromium of 0.25 % |
Copper | 0.2 % Show Material materials with Copper of 0.2 % |
Iron | 0.25 % Show Material materials with Iron of 0.25 % |
Magnesium | 4 - 5.2 % Show Material materials with Magnesium of 4 - 5.2 % |
Manganese | 0.7 - 1 % Show Material materials with Manganese of 0.7 - 1 % |
Other | each 0.05, total 0.15, Rest Al |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % |
Zinc | 0.4 % Show Material materials with Zinc of 0.4 % |
Zirconium | 0.2 % Show Material materials with Zirconium of 0.2 % |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |