General
Property | Value | Temperature |
---|---|---|
Density | 2.68 - 2.69 g/cm³ Show Material materials with Density of 2.68 - 2.69 g/cm³ at 20.0 °C | 20.0 °C |
2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ at 23.0 °C | 23.0 °C | |
Mechanical
Property | Value | Temperature | Comment |
---|---|---|---|
Bending Fatigue Strength | 140 MPa Show Material materials with Bending Fatigue Strength of 140 MPa at 23.0 °C | 23.0 °C | |
Elastic modulus | 70.5 GPa Show Material materials with Elastic modulus of 70.5 GPa at 20.0 °C | 20.0 °C | |
70.5 GPa Show Material materials with Elastic modulus of 70.5 GPa at 23.0 °C | 23.0 °C | ||
Elongation | 4 % Show Material materials with Elongation of 4 % at 20.0 °C | 20.0 °C | |
Elongation A100 | 4 % Show Material materials with Elongation A100 of 4 % at 23.0 °C | 23.0 °C | |
Plane-Strain Fracture Toughnes | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C | 23.0 °C | Typical for Wrought 5000 Series Aluminium |
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] at 20.0 °C | 20.0 °C | |
Shear modulus | 26.5 - 27 GPa Show Material materials with Shear modulus of 26.5 - 27 GPa at 20.0 °C | 20.0 °C | |
26.5 GPa Show Material materials with Shear modulus of 26.5 GPa at 23.0 °C | 23.0 °C | ||
Tensile strength | 290 MPa Show Material materials with Tensile strength of 290 MPa at 20.0 °C | 20.0 °C | |
290 MPa Show Material materials with Tensile strength of 290 MPa at 23.0 °C | 23.0 °C | ||
Yield strength Rp0.2 | 260 MPa Show Material materials with Yield strength Rp0.2 of 260 MPa at 20.0 °C | 20.0 °C | |
260 MPa Show Material materials with Yield strength Rp0.2 of 260 MPa at 23.0 °C | 23.0 °C | ||
Thermal
Property | Value | Temperature | Comment |
---|---|---|---|
Coefficient of thermal expansion | 2.19E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.19E-5 1/K at -50.0 °C | -50.0 °C | |
2.19E-5 - 2.56E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.19E-5 - 2.56E-5 1/K at 20.0 °C | 20.0 °C | ||
2.36E-5 - 2.37E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.36E-5 - 2.37E-5 1/K at 100.0 °C | 100.0 °C | ||
2.46E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.46E-5 1/K at 200.0 °C | 200.0 °C | ||
2.56E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.56E-5 1/K at 300.0 °C | 300.0 °C | ||
Max service temperature | 150 °C Show Material materials with Max service temperature of 150 °C | Typical for Wrought 5000 Series Aluminium | |
Melting point | 602 - 646 °C Show Material materials with Melting point of 602 - 646 °C | ||
Specific heat capacity | 897 - 900 J/(kg·K) Show Material materials with Specific heat capacity of 897 - 900 J/(kg·K) at 20.0 °C | 20.0 °C | |
900 J/(kg·K) Show Material materials with Specific heat capacity of 900 J/(kg·K) at 23.0 °C | 23.0 °C | ||
Thermal conductivity | 135 - 150 W/(m·K) Show Material materials with Thermal conductivity of 135 - 150 W/(m·K) at 20.0 °C | 20.0 °C | |
130 - 150 W/(m·K) Show Material materials with Thermal conductivity of 130 - 150 W/(m·K) at 23.0 °C | 23.0 °C | ||
Electrical
Property | Value | Temperature |
---|---|---|
Electrical conductivity | 2.10E+7 S/m Show Material materials with Electrical conductivity of 2.10E+7 S/m at 20.0 °C | 20.0 °C |
1.90E+7 - 2.10E+7 S/m Show Material materials with Electrical conductivity of 1.90E+7 - 2.10E+7 S/m at 23.0 °C | 23.0 °C | |
Electrical resistivity | 5.1E-8 Ω·m Show Material materials with Electrical resistivity of 5.1E-8 Ω·m at 20.0 °C | 20.0 °C |
4.76E-8 - 5.26E-8 Ω·m Show Material materials with Electrical resistivity of 4.76E-8 - 5.26E-8 Ω·m at 23.0 °C | 23.0 °C | |
Chemical properties
Property | ||
---|---|---|
Chromium | 0.05 - 0.2 % | |
Copper | 0.1 % | |
Iron | 0.4 % | |
Magnesium | 2.4 - 3 % | |
Manganese | 0.5 - 1 % | |
Other | Be < 0.0003 for welding additives, each 0.05, total 0.15, Rest Al | |
Silicon | 0.25 % | |
Titanium | 0.2 % | |
Zinc | 0.25 % |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: sufficient, Protective: good | |
Brazing | hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor | |
Corrosion properties | Seawater: very good, weathering: very good | |
Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (H12) |