Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.67 g/cm³ Show Material materials with Density of 2.67 g/cm³ | H112 | AA Standards, ASTM B209 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H112 | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 170.0 MPa Show Material materials with Tensile strength of 170.0 MPa | H112 | AA Standards, ASTM B209 | |
190.0 MPa Show Material materials with Tensile strength of 190.0 MPa | H112 | AA Standards, ASTM B209 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H112 | AA Standards, ASTM B209 | |
100 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H112 | AA Standards, ASTM B209 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 605.0 - 650.0 °C Show Material materials with Melting point of 605.0 - 650.0 °C | H112 | AA Standards, ASTM B209 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 138 W/(m·K) Show Material materials with Thermal conductivity of 138 W/(m·K) | H112 | AA Standards, ASTM B209 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 20000000.0 S/m Show Material materials with Electrical conductivity of 20000000.0 S/m | H112 | AA Standards, ASTM B209 |
Electrical resistivity | 5e-08 Ω·m Show Material materials with Electrical resistivity of 5e-08 Ω·m | H112 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.15 - 0.35 % Show Material materials with Chromium of 0.15 - 0.35 % | H112 | AA Standards, ASTM B209 |
Copper | 0.04 % Show Material materials with Copper of 0.04 % | H112 | AA Standards, ASTM B209 |
Magnesium | 2.2 - 2.8 % Show Material materials with Magnesium of 2.2 - 2.8 % | H112 | AA Standards, ASTM B209 |
Manganese | 0.01 % Show Material materials with Manganese of 0.01 % | H112 | AA Standards, ASTM B209 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H112 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: limited brazing | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |