EN 573-3 Grade AW-1100 H19

Want to keep this datasheet? Save it now in your required format

Description

Material EN AW-Al 99,0Cu is produced in large quantities for rolled bars and for prematerial for heat-exchanger. It is used in limited quantity for sheets, bands and plates, for foil and for pressed and drawing products as well as for pressed bars. This material is food-safe.

Related Standards

Equivalent Materials

This material data has been provided by WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Temperature
Density	2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ at 23.0 °C	23.0 °C

Mechanical

Property	Value	Temperature	Comment
Elastic modulus	69 GPa Show Material materials with Elastic modulus of 69 GPa at 23.0 °C	23.0 °C
Elongation A100	1 % Show Material materials with Elongation A100 of 1 % at 20.0 °C	20.0 °C
Elongation A50	1 % Show Material materials with Elongation A50 of 1 % at 20.0 °C	20.0 °C
	1 % Show Material materials with Elongation A50 of 1 % at 23.0 °C	23.0 °C

Plane-Strain Fracture Toughnes	22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C	23.0 °C	Typical for Wrought 1000 Series Aluminium
Poisson's ratio	0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C	23.0 °C	Typical for Wrought 1000 Series Aluminium
Shear modulus	25.9 GPa Show Material materials with Shear modulus of 25.9 GPa at 23.0 °C	23.0 °C	Typical for Wrought 1000 Series Aluminium
Tensile strength	180 MPa Show Material materials with Tensile strength of 180 MPa at 20.0 °C	20.0 °C
	180 MPa Show Material materials with Tensile strength of 180 MPa at 23.0 °C	23.0 °C
	Unlock all property charts
Yield strength Rp0.2	160 MPa Show Material materials with Yield strength Rp0.2 of 160 MPa at 20.0 °C	20.0 °C
	160 MPa Show Material materials with Yield strength Rp0.2 of 160 MPa at 23.0 °C	23.0 °C
	Unlock all property charts

Thermal

Property	Value	Temperature	Comment
Coefficient of thermal expansion	2.36E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.36E-5 1/K at 20.0 °C	20.0 °C
	2.36E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.36E-5 1/K at 100.0 °C	100.0 °C
	Unlock all property charts
Melting point	640 - 655 °C Show Material materials with Melting point of 640 - 655 °C
Specific heat capacity	900 - 963 J/(kg·K) Show Material materials with Specific heat capacity of 900 - 963 J/(kg·K) at 23.0 °C	23.0 °C	Typical for Wrought 1000 Series Aluminium
Thermal conductivity	218 - 222 W/(m·K) Show Material materials with Thermal conductivity of 218 - 222 W/(m·K) at 23.0 °C	23.0 °C

Electrical

Property	Value	Temperature
Electrical conductivity	3.30E+7 - 3.40E+7 S/m Show Material materials with Electrical conductivity of 3.30E+7 - 3.40E+7 S/m at 23.0 °C	23.0 °C
Electrical resistivity	2.94E-8 - 3.03E-8 Ω·m Show Material materials with Electrical resistivity of 2.94E-8 - 3.03E-8 Ω·m at 23.0 °C	23.0 °C

Chemical properties

Property
Aluminium	99 %
Copper	0.05 - 0.2 %
Manganese	0.05 %
Other		Be < 0.0008 for welding additives, each 0.05, total 0.15
Zinc	0.1 %

Technological properties

Property
Brazing	Excellent
Workability	Excellent workability.