AA Standards Grade 1100 H22

Want to keep this datasheet? Save it now in your required format

Description

AA 1100 is a soft, non-heat-treatable and low strength alloy that offers strong corrosion resistance. Composed of 99% aluminum and 0.12% copper, AA 1100 is purest grade of aluminum alloy available commercially.

Related Standards

Equivalent Materials

This material data has been provided by AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.71 g/cm³

Show Material materials with Density of 2.71 g/cm³

H22

AA Standards, ASTM B209

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Elastic modulus

69.0 GPa

Show Material materials with Elastic modulus of 69.0 GPa

H22

AA Standards, ASTM B209

Unlock all property charts

Elongation A100

23.0 °C

9 %

Show Material materials with Elongation A100 of 9 %

Elongation A50

23.0 °C

3 - 10 %

Show Material materials with Elongation A50 of 3 - 10 %

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 1000 Series Aluminium

Unlock all property charts

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 1000 Series Aluminium

Unlock all property charts

Shear modulus

25.9 GPa

Show Material materials with Shear modulus of 25.9 GPa

Typical for Wrought 1000 Series Aluminium

Unlock all property charts

Tensile strength

95.0 - 130.0 MPa

Show Material materials with Tensile strength of 95.0 - 130.0 MPa

H22

AA Standards, ASTM B209

Unlock all property charts

Yield strength Rp0.2

23.0 °C

75 MPa

Show Material materials with Yield strength Rp0.2 of 75 MPa

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

100 °C, 20 °C

2.36e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K

H22

AA Standards, ASTM B209

Unlock all property charts

Melting point

640.0 - 655.0 °C

Show Material materials with Melting point of 640.0 - 655.0 °C

H22

AA Standards, ASTM B209

Specific heat capacity

900.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 - 963.0 J/(kg·K)

Typical for Wrought 1000 Series Aluminium

Unlock all property charts

Thermal conductivity

218.0 - 222.0 W/(m·K)

Show Material materials with Thermal conductivity of 218.0 - 222.0 W/(m·K)

H22

AA Standards, ASTM B209

Unlock all property charts

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

33000000.0 - 34000000.0 S/m

Show Material materials with Electrical conductivity of 33000000.0 - 34000000.0 S/m

H22

AA Standards, ASTM B209

Unlock all property charts

Electrical resistivity

2.94e-08 - 3.03e-08 Ω·m

Show Material materials with Electrical resistivity of 2.94e-08 - 3.03e-08 Ω·m

H22

AA Standards, ASTM B209

Unlock all property charts

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

99.0 %

Show Material materials with Aluminium of 99.0 %

H22

AA Standards, ASTM B209

Copper

0.05 - 0.2 %

Show Material materials with Copper of 0.05 - 0.2 %

H22

AA Standards, ASTM B209

Manganese

0.05 %

Show Material materials with Manganese of 0.05 %

H22

AA Standards, ASTM B209

Other

each 0.05, total 0.15, Si + Fe < 0.95

Zinc

0.1 %

Show Material materials with Zinc of 0.1 %

H22

AA Standards, ASTM B209

Technological properties

Property
Brazing

general: possible with commercial processes and methods

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O, H12), poor (H14, H16, H18)

Workability

general (condition): good (O, H12, H14), acceptable (H16), poor(H18)