AA Standards Grade 1100 O

Want to keep this datasheet? Save it now in your required format

Description

AA 1100 is a soft, non-heat-treatable and low strength alloy that offers strong corrosion resistance. Composed of 99% aluminum and 0.12% copper, AA 1100 is purest grade of aluminum alloy available commercially.

Related Standards

Equivalent Materials

This material data has been provided by AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.71 g/cm³

Show Material materials with Density of 2.71 g/cm³

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Mechanical

PropertyValueConditionRelated StandardsComment

Bending Fatigue Strength

35.0 MPa

Show Material materials with Bending Fatigue Strength of 35.0 MPa

O

AA Standards

Elastic modulus

69.0 GPa

Show Material materials with Elastic modulus of 69.0 GPa

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Hardness, Brinell

23.0 [-]

Show Material materials with Hardness, Brinell of 23.0 [-]

O

AA Standards

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 1000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 1000 Series Aluminium

Shear modulus

25.9 GPa

Show Material materials with Shear modulus of 25.9 GPa

Typical for Wrought 1000 Series Aluminium

Tensile strength

75.0 - 105.0 MPa

Show Material materials with Tensile strength of 75.0 - 105.0 MPa

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B547

75.0 MPa

Show Material materials with Tensile strength of 75.0 MPa

O

AA Standards, ASTM B483

90.0 MPa

Show Material materials with Tensile strength of 90.0 MPa

O

AA Standards

110.0 MPa

Show Material materials with Tensile strength of 110.0 MPa

O

AA Standards, ASTM B316

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

20 °C

2.36e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

100 °C

2.36e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Melting point

640.0 - 655.0 °C

Show Material materials with Melting point of 640.0 - 655.0 °C

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Specific heat capacity

900.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 - 963.0 J/(kg·K)

Typical for Wrought 1000 Series Aluminium

Thermal conductivity

218.0 - 222.0 W/(m·K)

Show Material materials with Thermal conductivity of 218.0 - 222.0 W/(m·K)

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

33000000.0 - 34000000.0 S/m

Show Material materials with Electrical conductivity of 33000000.0 - 34000000.0 S/m

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Electrical resistivity

2.94e-08 - 3.03e-08 Ω·m

Show Material materials with Electrical resistivity of 2.94e-08 - 3.03e-08 Ω·m

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

99.0 %

Show Material materials with Aluminium of 99.0 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Copper

0.05 - 0.2 %

Show Material materials with Copper of 0.05 - 0.2 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Manganese

0.05 %

Show Material materials with Manganese of 0.05 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Zinc

0.1 %

Show Material materials with Zinc of 0.1 %

O

AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Technological properties

Property
Brazing

general: possible with commercial processes and methods

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O, H12), poor (H14, H16, H18)

Workability

general (condition): good (O, H12, H14), acceptable (H16), poor(H18)