Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | T651 | AA Standards |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 110.0 MPa Show Material materials with Bending Fatigue Strength of 110.0 MPa | T651 | AA Standards | |
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | T651 | AA Standards | |
Hardness, Brinell | 120.0 [-] Show Material materials with Hardness, Brinell of 120.0 [-] | T651 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Tensile strength | 395.0 MPa Show Material materials with Tensile strength of 395.0 MPa | T651 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3199999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K | T651 | AA Standards | |
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K | T651 | AA Standards | ||
Melting point | 560.0 - 645.0 °C Show Material materials with Melting point of 560.0 - 645.0 °C | T651 | AA Standards | ||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Thermal conductivity | 146.0 - 155.0 W/(m·K) Show Material materials with Thermal conductivity of 146.0 - 155.0 W/(m·K) | T651 | AA Standards |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 21000000.0 - 23000000.0 S/m Show Material materials with Electrical conductivity of 21000000.0 - 23000000.0 S/m | T651 | AA Standards |
Electrical resistivity | 4.35e-08 - 4.76e-08 Ω·m Show Material materials with Electrical resistivity of 4.35e-08 - 4.76e-08 Ω·m | T651 | AA Standards |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.4 % Show Material materials with Chromium of 0.4 % | T651 | AA Standards |
Copper | 0.7 - 1.2 % Show Material materials with Copper of 0.7 - 1.2 % | T651 | AA Standards |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | T651 | AA Standards |
Magnesium | 0.8 - 1.4 % Show Material materials with Magnesium of 0.8 - 1.4 % | T651 | AA Standards |
Manganese | 0.6 - 1.1 % Show Material materials with Manganese of 0.6 - 1.1 % | T651 | AA Standards |
Silicon | 0.9 - 1.8 % Show Material materials with Silicon of 0.9 - 1.8 % | T651 | AA Standards |
Titanium | 0.2 % Show Material materials with Titanium of 0.2 % | T651 | AA Standards |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T651 | AA Standards |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O), no damage during operation, limited damage during laboratory tests, general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O), sufficient (T4, T4510, T4511), good to acceptable (T6, T6510, T6511) | |
| Workability | general (condition): acceptable (O), poor(T4, T4510, T4511, T6, T6510, T6511) | |