Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | T61 | AA Standards, ASTM B317 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | T61 | AA Standards, ASTM B317 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Tensile strength | 105.0 MPa Show Material materials with Tensile strength of 105.0 MPa | T61 | AA Standards, ASTM B317 | |
125.0 MPa Show Material materials with Tensile strength of 125.0 MPa | T61 | AA Standards, ASTM B317 | ||
140.0 MPa Show Material materials with Tensile strength of 140.0 MPa | T61 | AA Standards, ASTM B317 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T61 | AA Standards, ASTM B317 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T61 | AA Standards, ASTM B317 | ||
Melting point | 620.0 - 655.0 °C Show Material materials with Melting point of 620.0 - 655.0 °C | T61 | AA Standards, ASTM B317 | ||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Thermal conductivity | 218.0 - 226.0 W/(m·K) Show Material materials with Thermal conductivity of 218.0 - 226.0 W/(m·K) | T61 | AA Standards, ASTM B317 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 33000000.0 - 35000000.0 S/m Show Material materials with Electrical conductivity of 33000000.0 - 35000000.0 S/m | T61 | AA Standards, ASTM B317 |
Electrical resistivity | 2.86e-08 - 3.03e-08 Ω·m Show Material materials with Electrical resistivity of 2.86e-08 - 3.03e-08 Ω·m | T61 | AA Standards, ASTM B317 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Boron | 0.06 % Show Material materials with Boron of 0.06 % | T61 | AA Standards, ASTM B317 |
Chromium | 0.03 % Show Material materials with Chromium of 0.03 % | T61 | AA Standards, ASTM B317 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | T61 | AA Standards, ASTM B317 |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | T61 | AA Standards, ASTM B317 |
Magnesium | 0.35 - 0.8 % Show Material materials with Magnesium of 0.35 - 0.8 % | T61 | AA Standards, ASTM B317 |
Manganese | 0.03 % Show Material materials with Manganese of 0.03 % | T61 | AA Standards, ASTM B317 |
Silicon | 0.3 - 0.7 % Show Material materials with Silicon of 0.3 - 0.7 % | T61 | AA Standards, ASTM B317 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T61 | AA Standards, ASTM B317 |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: sufficient (T6, T63), poor (T61, T64) | |
Workability | general (condition): poor(T6, T63), acceptable (T61, T64) |