Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 90.0 MPa Show Material materials with Bending Fatigue Strength of 90.0 MPa | T9 | AA Standards | |
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | Typical for Wrought 6000 Series Aluminium | ||
Hardness, Brinell | 120.0 [-] Show Material materials with Hardness, Brinell of 120.0 [-] | T9 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Tensile strength | 330.0 MPa Show Material materials with Tensile strength of 330.0 MPa | T9 | AA Standards, ASTM B210, ASTM B483 | |
345.0 MPa Show Material materials with Tensile strength of 345.0 MPa | T9 | AA Standards, ASTM B211 | ||
360.0 MPa Show Material materials with Tensile strength of 360.0 MPa | T9 | AA Standards, ASTM B211 | ||
400.0 MPa Show Material materials with Tensile strength of 400.0 MPa | T9 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 | ||
Melting point | 580.0 - 650.0 °C Show Material materials with Melting point of 580.0 - 650.0 °C | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 | ||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Thermal conductivity | 172 W/(m·K) Show Material materials with Thermal conductivity of 172 W/(m·K) | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 26000000.0 S/m Show Material materials with Electrical conductivity of 26000000.0 S/m | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Electrical resistivity | 3.85e-08 Ω·m Show Material materials with Electrical resistivity of 3.85e-08 Ω·m | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Bismuth | 0.4 - 0.7 % Show Material materials with Bismuth of 0.4 - 0.7 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Chromium | 0.04 - 0.14 % Show Material materials with Chromium of 0.04 - 0.14 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Copper | 0.15 - 0.4 % Show Material materials with Copper of 0.15 - 0.4 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Lead | 0.4 - 0.7 % Show Material materials with Lead of 0.4 - 0.7 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Magnesium | 0.8 - 1.2 % Show Material materials with Magnesium of 0.8 - 1.2 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Manganese | 0.15 % Show Material materials with Manganese of 0.15 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Silicon | 0.4 - 0.8 % Show Material materials with Silicon of 0.4 - 0.8 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T9 | AA Standards, ASTM B210, ASTM B211, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: good to acceptable (T6, T651, T6510, T6511, T9) | |
| Workability | general (condition): poor(T6, T651, T6510, T6511), not suitable (T9) | |