Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | T1 | AA Standards, ASTM B221 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | Typical for Wrought 6000 Series Aluminium | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Tensile strength | 170.0 MPa Show Material materials with Tensile strength of 170.0 MPa | T1 | AA Standards, ASTM B221 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | T1 | AA Standards, ASTM B221 | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | T1 | AA Standards, ASTM B221 | ||
Melting point | 605.0 - 655.0 °C Show Material materials with Melting point of 605.0 - 655.0 °C | T1 | AA Standards, ASTM B221 | ||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Thermal conductivity | 180.0 - 188.0 W/(m·K) Show Material materials with Thermal conductivity of 180.0 - 188.0 W/(m·K) | T1 | AA Standards, ASTM B221 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 27000000.0 - 28000000.0 S/m Show Material materials with Electrical conductivity of 27000000.0 - 28000000.0 S/m | T1 | AA Standards, ASTM B221 |
Electrical resistivity | 3.57e-08 - 3.7e-08 Ω·m Show Material materials with Electrical resistivity of 3.57e-08 - 3.7e-08 Ω·m | T1 | AA Standards, ASTM B221 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T1 | AA Standards, ASTM B221 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | T1 | AA Standards, ASTM B221 |
Iron | 0.35 % Show Material materials with Iron of 0.35 % | T1 | AA Standards, ASTM B221 |
Magnesium | 0.4 - 0.6 % Show Material materials with Magnesium of 0.4 - 0.6 % | T1 | AA Standards, ASTM B221 |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | T1 | AA Standards, ASTM B221 |
Silicon | 0.6 - 0.9 % Show Material materials with Silicon of 0.6 - 0.9 % | T1 | AA Standards, ASTM B221 |
Titanium | 0.1 % Show Material materials with Titanium of 0.1 % | T1 | AA Standards, ASTM B221 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T1 | AA Standards, ASTM B221 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Workability | Excellent workability. | |