Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 68 - 70 GPa Show Material materials with Elastic modulus of 68 - 70 GPa at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Elongation A50 | 15 % Show Material materials with Elongation A50 of 15 % at 23.0 °C | 23.0 °C | |
Plane-Strain Fracture Toughnes | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Tensile strength | 125 - 145 MPa Show Material materials with Tensile strength of 125 - 145 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 2.2E-5 - 2.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.2E-5 - 2.5E-5 1/K at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Melting point | 645 - 660 °C Show Material materials with Melting point of 645 - 660 °C | Typical for Wrought 1000 Series Aluminium | |
Specific heat capacity | 900 - 963 J/(kg·K) Show Material materials with Specific heat capacity of 900 - 963 J/(kg·K) at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Thermal conductivity | 167 - 244 W/(m·K) Show Material materials with Thermal conductivity of 167 - 244 W/(m·K) at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Electrical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Electrical conductivity | 3.30E+7 - 3.80E+7 S/m Show Material materials with Electrical conductivity of 3.30E+7 - 3.80E+7 S/m at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Electrical resistivity | 2.7E-8 - 3E-8 Ω·m Show Material materials with Electrical resistivity of 2.7E-8 - 3E-8 Ω·m at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Chemical properties
| Property | ||
|---|---|---|
Aluminium | 99.1 % | |
Boron | 0.02 % | |
Chromium | 0.01 % | |
Copper | 0.04 % | |
Iron | 0.8 % | |
Magnesium | 0.25 % | |
Manganese | 0.01 % | |
Other | Ti + V < 0.03, each 0.03, total 0.15 | |
Silicon | 0.3 % |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |
| Workability | Excellent workability. | |