General
Property | Value | Temperature |
---|---|---|
Density | 2.71 - 2.72 g/cm³ Show Material materials with Density of 2.71 - 2.72 g/cm³ at 20.0 °C | 20.0 °C |
2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ at 23.0 °C | 23.0 °C | |
Mechanical
Property | Value | Temperature | Comment |
---|---|---|---|
Elastic modulus | 60 - 69 GPa Show Material materials with Elastic modulus of 60 - 69 GPa at 20.0 °C | 20.0 °C | |
69 GPa Show Material materials with Elastic modulus of 69 GPa at 23.0 °C | 23.0 °C | ||
Elongation | 16 - 20 % Show Material materials with Elongation of 16 - 20 % at 20.0 °C | 20.0 °C | |
Elongation A100 | 16 - 20 % Show Material materials with Elongation A100 of 16 - 20 % at 23.0 °C | 23.0 °C | |
Elongation A50 | 16 - 18 % Show Material materials with Elongation A50 of 16 - 18 % at 20.0 °C | 20.0 °C | |
16 - 18 % Show Material materials with Elongation A50 of 16 - 18 % at 23.0 °C | 23.0 °C | ||
Elongation A50, transverse | 16 % Show Material materials with Elongation A50, transverse of 16 % at 20.0 °C | 20.0 °C | |
Elongation, transverse | 16 % Show Material materials with Elongation, transverse of 16 % at 20.0 °C | 20.0 °C | |
Hardness, Brinell | 23 - 26 [-] Show Material materials with Hardness, Brinell of 23 - 26 [-] at 20.0 °C | 20.0 °C | |
24 - 26 [-] Show Material materials with Hardness, Brinell of 24 - 26 [-] at 23.0 °C | 23.0 °C | ||
Plane-Strain Fracture Toughnes | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C | 23.0 °C | Typical for Wrought 1000 Series Aluminium |
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] at 20.0 °C | 20.0 °C | |
Shear modulus | 24 - 26 GPa Show Material materials with Shear modulus of 24 - 26 GPa at 20.0 °C | 20.0 °C | |
25.9 GPa Show Material materials with Shear modulus of 25.9 GPa at 23.0 °C | 23.0 °C | ||
Tensile strength | 75 - 85 MPa Show Material materials with Tensile strength of 75 - 85 MPa at 20.0 °C | 20.0 °C | |
75 - 85 MPa Show Material materials with Tensile strength of 75 - 85 MPa at 23.0 °C | 23.0 °C | ||
Tensile strength, transverse | 80 - 85 MPa Show Material materials with Tensile strength, transverse of 80 - 85 MPa at 20.0 °C | 20.0 °C | |
Yield strength Rp0.2 | 25 - 35 MPa Show Material materials with Yield strength Rp0.2 of 25 - 35 MPa at 20.0 °C | 20.0 °C | |
25 - 35 MPa Show Material materials with Yield strength Rp0.2 of 25 - 35 MPa at 23.0 °C | 23.0 °C | ||
Yield strength Rp0.2, transverse | 30 - 35 MPa Show Material materials with Yield strength Rp0.2, transverse of 30 - 35 MPa at 20.0 °C | 20.0 °C |
Thermal
Property | Value | Temperature |
---|---|---|
Coefficient of thermal expansion | 2.17E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.17E-5 1/K at -50.0 °C | -50.0 °C |
2.17E-5 - 2.54E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.17E-5 - 2.54E-5 1/K at 20.0 °C | 20.0 °C | |
2.35E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.35E-5 1/K at 100.0 °C | 100.0 °C | |
2.44E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.44E-5 1/K at 200.0 °C | 200.0 °C | |
2.54E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.54E-5 1/K at 300.0 °C | 300.0 °C | |
Melting point | 644 - 657 °C Show Material materials with Melting point of 644 - 657 °C | |
Specific heat capacity | 898 J/(kg·K) Show Material materials with Specific heat capacity of 898 J/(kg·K) at 20.0 °C | 20.0 °C |
Thermal conductivity | 205 - 225 W/(m·K) Show Material materials with Thermal conductivity of 205 - 225 W/(m·K) at 20.0 °C | 20.0 °C |
205 - 210 W/(m·K) Show Material materials with Thermal conductivity of 205 - 210 W/(m·K) at 23.0 °C | 23.0 °C | |
Electrical
Property | Value | Temperature |
---|---|---|
Electrical conductivity | 3.44E+7 - 3.55E+7 S/m Show Material materials with Electrical conductivity of 3.44E+7 - 3.55E+7 S/m at 20.0 °C | 20.0 °C |
3.30E+7 - 3.40E+7 S/m Show Material materials with Electrical conductivity of 3.30E+7 - 3.40E+7 S/m at 23.0 °C | 23.0 °C | |
Electrical resistivity | 2.95E-8 Ω·m Show Material materials with Electrical resistivity of 2.95E-8 Ω·m at 20.0 °C | 20.0 °C |
2.94E-8 - 3.03E-8 Ω·m Show Material materials with Electrical resistivity of 2.94E-8 - 3.03E-8 Ω·m at 23.0 °C | 23.0 °C | |
Chemical properties
Property | ||
---|---|---|
Aluminium | 99 % | |
Copper | 0.05 % | |
Manganese | 0.05 % | |
Other | Si + Fe < 1.00, each 0.05, total 0.15 | |
Titanium | 0.05 % | |
Zinc | 0.1 % |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: acceptable, Protective: very good | |
Brazing | hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good | |
Corrosion properties | Seawater: sufficient, weathering: acceptable | |
Workability | Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H12) / very good (H12) |