Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 95.0 MPa Show Material materials with Bending Fatigue Strength of 95.0 MPa | T651 | AA Standards | |
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |
Hardness, Brinell | 95.0 [-] Show Material materials with Hardness, Brinell of 95.0 [-] | T651 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Tensile strength | 275.0 MPa Show Material materials with Tensile strength of 275.0 MPa | T651 | AA Standards, ASTM B209 | |
290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | ||
310.0 MPa Show Material materials with Tensile strength of 310.0 MPa | T651 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | ||
Melting point | 580.0 - 650.0 °C Show Material materials with Melting point of 580.0 - 650.0 °C | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | ||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Thermal conductivity | 155.0 - 180.0 W/(m·K) Show Material materials with Thermal conductivity of 155.0 - 180.0 W/(m·K) | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 23000000.0 - 27000000.0 S/m Show Material materials with Electrical conductivity of 23000000.0 - 27000000.0 S/m | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Electrical resistivity | 3.7e-08 - 4.35e-08 Ω·m Show Material materials with Electrical resistivity of 3.7e-08 - 4.35e-08 Ω·m | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.04 - 0.35 % Show Material materials with Chromium of 0.04 - 0.35 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Copper | 0.15 - 0.4 % Show Material materials with Copper of 0.15 - 0.4 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Magnesium | 0.8 - 1.2 % Show Material materials with Magnesium of 0.8 - 1.2 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Manganese | 0.15 % Show Material materials with Manganese of 0.15 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Silicon | 0.4 - 0.8 % Show Material materials with Silicon of 0.4 - 0.8 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, T6, T651, T652, T6510, T6511), no damage during operation, limited damage during laboratory tests (T4, T451, T4510, T4511), general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O), sufficient (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) | |
| Workability | general (condition): good (O), acceptable (T4, T451, T4510, T4511), poor(T6, T651, T652, T6510, T6511) | |