General
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | T89 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | ||
20.0 °C | 68.0 - 73.0 GPa Show Material materials with Elastic modulus of 68.0 - 73.0 GPa | T89 | EN 573-3 | Wire | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||||
Shear modulus | 26.4 GPa Show Material materials with Shear modulus of 26.4 GPa | T89 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | ||
20.0 °C | 26.0 - 27.0 GPa Show Material materials with Shear modulus of 26.0 - 27.0 GPa | T89 | EN 573-3 | Wire | ||
Tensile strength | 340.0 MPa Show Material materials with Tensile strength of 340.0 MPa | T89 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | ||
20.0 °C | 340.0 MPa Show Material materials with Tensile strength of 340.0 MPa | T89 | EN 573-3 | Wire |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T89 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T89 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | |
Melting point | 585.0 - 650.0 °C Show Material materials with Melting point of 585.0 - 650.0 °C | T89 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | |
Specific heat capacity | 896.0 J/(kg·K) Show Material materials with Specific heat capacity of 896.0 J/(kg·K) | T89 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | |
Thermal conductivity | 20.0 °C | 170.0 - 220.0 W/(m·K) Show Material materials with Thermal conductivity of 170.0 - 220.0 W/(m·K) | T89 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Forging, Tube, Bar |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 24000000.0 - 32000000.0 S/m Show Material materials with Electrical conductivity of 24000000.0 - 32000000.0 S/m | T89 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Forging, Tube, Bar |
Electrical resistivity | 3.13e-08 - 4.17e-08 Ω·m Show Material materials with Electrical resistivity of 3.13e-08 - 4.17e-08 Ω·m | T89 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Chromium | 0.25 % Show Material materials with Chromium of 0.25 % | T89 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Forging, Tube, Bar |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | T89 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Forging, Tube, Bar |
Iron | 0.5 % Show Material materials with Iron of 0.5 % | T89 | EN 573-3 | Wire |
0.50 % Show Material materials with Iron of 0.50 % | T89 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Forging, Tube, Bar | |
Magnesium | 0.6 - 1.2 % Show Material materials with Magnesium of 0.6 - 1.2 % | T89 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Forging, Tube, Bar |
Manganese | 0.4 - 1.0 % Show Material materials with Manganese of 0.4 - 1.0 % | T89 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Forging, Tube, Bar |
Silicon | 0.7 - 1.3 % Show Material materials with Silicon of 0.7 - 1.3 % | T89 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Forging, Tube, Bar |
Titanium | 0.1 % Show Material materials with Titanium of 0.1 % | T89 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Forging, Tube, Bar |
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % | T89 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Forging, Tube, Bar |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: acceptable, Protective: very good | |
Brazing | hard brazing (with flux/ without flux): good / sufficient, friction soldering: good, soft brazing with flux: acceptable | |
Corrosion properties | Seawater: good, weathering: very good | |
Workability | Bending / Spinning (cold): acceptable (T3, T4) / good (O), Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) good (O) / good (O) |