EN 573-3 Grade AW-1350 H112

Want to keep this datasheet? Save it now in your required format

Description

Material EN AW-EAl 99,5 is produced in high amount for wire and prewire for electrotechnical applications as well as for extruded components and drawn parts. The alloy is food-safe.

Related Standards

Equivalent Materials

This material data has been provided by WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperature

Density

2.7 - 2.71 g/cm³

Show Material materials with Density of 2.7 - 2.71 g/cm³ at 23.0 °C

23.0 °C

Mechanical

PropertyValueTemperatureComment

Elastic modulus

69 - 70 GPa

Show Material materials with Elastic modulus of 69 - 70 GPa at 23.0 °C

23.0 °C

Elongation

25 %

Show Material materials with Elongation of 25 % at 20.0 °C

20.0 °C

20 %

Show Material materials with Elongation of 20 % at 23.0 °C

23.0 °C

Elongation A100

25 %

Show Material materials with Elongation A100 of 25 % at 23.0 °C

23.0 °C

Elongation A50

23 %

Show Material materials with Elongation A50 of 23 % at 20.0 °C

20.0 °C

20 - 23 %

Show Material materials with Elongation A50 of 20 - 23 % at 23.0 °C

23.0 °C

Unlock all property charts

Hardness, Brinell

23 [-]

Show Material materials with Hardness, Brinell of 23 [-] at 23.0 °C

23.0 °C

Plane-Strain Fracture Toughnes

22 - 35 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C

23.0 °C

Typical for Wrought 1000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C

23.0 °C

Typical for Wrought 1000 Series Aluminium

Shear modulus

25.9 GPa

Show Material materials with Shear modulus of 25.9 GPa at 23.0 °C

23.0 °C

Typical for Wrought 1000 Series Aluminium

Tensile strength

60 MPa

Show Material materials with Tensile strength of 60 MPa at 20.0 °C

20.0 °C

60 - 75 MPa

Show Material materials with Tensile strength of 60 - 75 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Yield strength Rp0.2

60 MPa

Show Material materials with Yield strength Rp0.2 of 60 MPa at 20.0 °C

20.0 °C

30 MPa

Show Material materials with Yield strength Rp0.2 of 30 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Thermal

PropertyValueTemperatureComment

Coefficient of thermal expansion

2.36E-5 - 2.38E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.36E-5 - 2.38E-5 1/K at 20.0 °C

20.0 °C

2.36E-5 - 2.38E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.36E-5 - 2.38E-5 1/K at 100.0 °C

100.0 °C

Unlock all property charts

Melting point

645 - 657 °C

Show Material materials with Melting point of 645 - 657 °C

Specific heat capacity

900 - 963 J/(kg·K)

Show Material materials with Specific heat capacity of 900 - 963 J/(kg·K) at 23.0 °C

23.0 °C

Typical for Wrought 1000 Series Aluminium

Thermal conductivity

225 - 235 W/(m·K)

Show Material materials with Thermal conductivity of 225 - 235 W/(m·K) at 23.0 °C

23.0 °C

Electrical

PropertyValueTemperature

Electrical conductivity

3.54E+7 - 3.65E+7 S/m

Show Material materials with Electrical conductivity of 3.54E+7 - 3.65E+7 S/m at 23.0 °C

23.0 °C

Electrical resistivity

2.74E-8 - 2.82E-8 Ω·m

Show Material materials with Electrical resistivity of 2.74E-8 - 2.82E-8 Ω·m at 23.0 °C

23.0 °C

Chemical properties

Property

Aluminium

99.5 %

Boron

0.05 %

Chromium

0.01 %

Copper

0.05 %

Gallium

0.03 %

Iron

0.4 %

Manganese

0.01 %

Other

Ti + V < 0.02, each 0.03, total 0.10

Silicon

0.1 %

Zinc

0.05 %

Technological properties

Property
Brazing

Excellent

Workability

Excellent workability.