General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 2.85 g/cm³ Show Material materials with Density of 2.85 g/cm³ | T3 | EN 573-3, EN 754 | Rod, Tube | |
20.0 °C | 2.85 g/cm³ Show Material materials with Density of 2.85 g/cm³ | T3 | EN 573-3 | Rod, Tube |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 72.5 GPa Show Material materials with Elastic modulus of 72.5 GPa | T3 | EN 573-3, EN 754 | Rod, Tube | ||
Elongation | 5.0 % Show Material materials with Elongation of 5.0 % | T3 | EN 573-3, EN 754 | Rod, Tube | A50 | |
6.0 % Show Material materials with Elongation of 6.0 % | T3 | EN 573-3, EN 754 | Rod, Tube | A100 | ||
7.0 % Show Material materials with Elongation of 7.0 % | T3 | EN 573-3, EN 754 | Rod, Tube | A100 | ||
20.0 °C | 5.0 % Show Material materials with Elongation of 5.0 % | T3 | EN 573-3 | Rod, Tube | A50 | |
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | T3 | EN 573-3 | Rod | ||
20.0 °C | 7.0 % Show Material materials with Elongation of 7.0 % | T3 | EN 573-3 | Tube, Rod | ||
Hardness, Brinell | 20.0 °C | 95.0 [-] Show Material materials with Hardness, Brinell of 95.0 [-] | T3 | EN 573-3 | Rod, Tube | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Shear modulus | 27.3 GPa Show Material materials with Shear modulus of 27.3 GPa | T3 | EN 573-3, EN 754 | Rod, Tube | ||
Tensile strength | 340.0 MPa Show Material materials with Tensile strength of 340.0 MPa | T3 | EN 573-3, EN 754 | Rod, Tube | ||
370.0 MPa Show Material materials with Tensile strength of 370.0 MPa | T3 | EN 573-3, EN 754 | Rod, Tube | |||
20.0 °C | 340.0 MPa Show Material materials with Tensile strength of 340.0 MPa | T3 | EN 573-3 | Rod | ||
20.0 °C | 370.0 MPa Show Material materials with Tensile strength of 370.0 MPa | T3 | EN 573-3 | Tube, Rod |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T3 | EN 573-3, EN 754 | Rod, Tube |
100 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T3 | EN 573-3, EN 754 | Rod, Tube | |
100.0 °C | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | T3 | EN 573-3 | Rod, Tube | |
Melting point | 507.0 - 650.0 °C Show Material materials with Melting point of 507.0 - 650.0 °C | T3 | EN 573-3, EN 754 | Rod, Tube | |
Specific heat capacity | 860.0 J/(kg·K) Show Material materials with Specific heat capacity of 860.0 J/(kg·K) | T3 | EN 573-3, EN 754 | Rod, Tube | |
20.0 °C | 860.0 J/(kg·K) Show Material materials with Specific heat capacity of 860.0 J/(kg·K) | T3 | EN 573-3 | Rod, Tube | |
Thermal conductivity | 130.0 - 160.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 - 160.0 W/(m·K) | T3 | EN 573-3, EN 754 | Rod, Tube | |
20.0 °C | 116.0 - 168.0 W/(m·K) Show Material materials with Thermal conductivity of 116.0 - 168.0 W/(m·K) | T3 | EN 573-3 | Rod, Tube |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 18000000.0 - 22000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 22000000.0 S/m | T3 | EN 573-3, EN 754 | Rod, Tube |
Electrical resistivity | 4.55e-08 - 5.56e-08 Ω·m Show Material materials with Electrical resistivity of 4.55e-08 - 5.56e-08 Ω·m | T3 | EN 573-3, EN 754 | Rod, Tube |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Bismuth | 0.2 % Show Material materials with Bismuth of 0.2 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Copper | 3.3 - 4.6 % Show Material materials with Copper of 3.3 - 4.6 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Iron | 0.8 % Show Material materials with Iron of 0.8 % | T3 | EN 573-3 | Rod, Tube |
0.80 % Show Material materials with Iron of 0.80 % | T3 | EN 573-3, EN 754 | Rod, Tube | |
Lead | 0.8 - 1.5 % Show Material materials with Lead of 0.8 - 1.5 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Magnesium | 0.4 - 1.8 % Show Material materials with Magnesium of 0.4 - 1.8 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Manganese | 0.5 - 1.0 % Show Material materials with Manganese of 0.5 - 1.0 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Nickel | 0.2 % Show Material materials with Nickel of 0.2 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Silicon | 0.8 % Show Material materials with Silicon of 0.8 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Tin | 0.2 % Show Material materials with Tin of 0.2 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Titanium | 0.2 % Show Material materials with Titanium of 0.2 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Zinc | 0.8 % Show Material materials with Zinc of 0.8 % | T3 | EN 573-3, EN 754 | Rod, Tube |
Technological properties
Property | ||
---|---|---|
Anodizing | Protective: poor | |
Brazing | friction soldering: sufficient | |
Corrosion properties | Seawater: poor, weathering: poor | |
Workability | Bending / Spinning (cold): sufficient / -, Deep drawing / upsetting (Condition) - / sufficient |