EN 573-3 Grade AW-2014 T451

Want to keep this datasheet? Save it now in your required format

Description

Age-hardenable AlCu alloy. The alloy is not food safe.

Related Standards

Equivalent Materials

Ashby charts

See where EN 573-3 Grade AW-2014 T451 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.8 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Mechanical

Bending angle 180°

θ180

3 - 5 °/t at 20 °C

Show 2000 Series materials with Bending angle 180° of 3 - 5 °/t at 20 °C

Bending angle 90°

θ90

3 - 8 °/t at 20 °C

Show 2000 Series materials with Bending angle 90° of 3 - 8 °/t at 20 °C

Elastic modulus

E

72 - 73 GPa at 20 °C

Show 2000 Series materials with Elastic modulus of 72 - 73 GPa at 20 °C

Elongation

A

7 - 12 % at 20 °C

Show 2000 Series materials with Elongation of 7 - 12 % at 20 °C

Elongation A100

A100

10 % at 20 °C

Show 2000 Series materials with Elongation A100 of 10 % at 20 °C

Elongation A50

A50

7 - 14 % at 20 °C

Show 2000 Series materials with Elongation A50 of 7 - 14 % at 20 °C

Elongation A50, transverse

A50,trans

14 % at 20 °C

Show 2000 Series materials with Elongation A50, transverse of 14 % at 20 °C

Elongation, transverse

A

7 - 10 % at 20 °C

Show 2000 Series materials with Elongation, transverse of 7 - 10 % at 20 °C

Hardness, Brinell

HB

110 - 112 [-] at 20 °C

Show 2000 Series materials with Hardness, Brinell of 110 - 112 [-] at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 2000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 2000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 2000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Typical for Wrought 2000 Series Aluminium

Shear modulus

G

27.4 GPa at 20 °C

Show 2000 Series materials with Shear modulus of 27.4 GPa at 20 °C

Tensile strength

Rm

380 - 400 MPa at 20 °C

Show 2000 Series materials with Tensile strength of 380 - 400 MPa at 20 °C

Tensile strength, transverse

Rm,trans

395 - 400 MPa at 20 °C

Show 2000 Series materials with Tensile strength, transverse of 395 - 400 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

220 - 250 MPa at 20 °C

Show 2000 Series materials with Yield strength Rp0.2 of 220 - 250 MPa at 20 °C

Yield strength Rp0.2, transverse

Rp0.2,trans

240 - 250 MPa at 20 °C

Show 2000 Series materials with Yield strength Rp0.2, transverse of 240 - 250 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.1E-5 1/K at -50 °C

Hide chart

Melting point

Tm

505 - 640 °C

Specific heat capacity

cp

816 - 963 J/(kg·K) at 20 °C

Typical for Wrought 2000 Series Aluminium

Thermal conductivity

λ

134 - 200 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.00E+7 - 2.90E+7 S/m at 20 °C

Electrical resistivity

ρel

3.45E-8 - 5E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Other

-

Cr + Ti < 0.20 for extruded products, if agreed., each 0.05, total 0.15, Rest Al

Cu

3.9 - 5 %

Fe

0.5 - 0.7 %

Si

0.5 - 1.2 %

Mn

0.4 - 1.2 %

More

Technological properties

Anodizing

decorative: not suitable, Protective: acceptable

Brazing

hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable

Corrosion properties

Seawater: sufficient, weathering: acceptable

Workability

Bending / Spinning (cold): gut (O) / ungeeignet, Impact extrusion (cold): not suitable, Deep drawing / upsetting (Condition) acceptable (O) / not suitable

This material data has been provided by WIAM,AluKey.