Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.75 g/cm³ Show Material materials with Density of 2.75 g/cm³ | H13 | EN 573-3, EN 1301 | Wire | |
20.0 °C | 2.74 g/cm³ Show Material materials with Density of 2.74 g/cm³ | H13 | EN 573-3 | Wire |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H13 | EN 573-3, EN 1301 | Wire | ||
20.0 °C | 67.0 GPa Show Material materials with Elastic modulus of 67.0 GPa | H13 | EN 573-3 | Wire | ||
Elongation | 5.0 % Show Material materials with Elongation of 5.0 % | H13 | EN 573-3, EN 1301 | Wire | ||
20.0 °C | 20.0 % Show Material materials with Elongation of 20.0 % | H13 | EN 573-3 | Wire | A100 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Shear modulus | 20.0 °C | 25.5 GPa Show Material materials with Shear modulus of 25.5 GPa | H13 | EN 573-3 | Wire | |
Tensile strength | 170.0 - 240.0 MPa Show Material materials with Tensile strength of 170.0 - 240.0 MPa | H13 | EN 573-3, EN 1301 | Wire | ||
20.0 °C | 260.0 MPa Show Material materials with Tensile strength of 260.0 MPa | H13 | EN 573-3 | Wire |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | -50.0 °C | 2.18e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.18e-05 1/K | H13 | EN 573-3 | Wire | |
100.0 °C | 2.34e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.34e-05 1/K | H13 | EN 573-3 | Wire | ||
200.0 °C | 2.45e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.45e-05 1/K | H13 | EN 573-3 | Wire | ||
300.0 °C | 2.56e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.56e-05 1/K | H13 | EN 573-3 | Wire | ||
Melting point | 500.0 - 650.0 °C Show Material materials with Melting point of 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium | ||||
Specific heat capacity | 20.0 °C | 898.0 J/(kg·K) Show Material materials with Specific heat capacity of 898.0 J/(kg·K) | H13 | EN 573-3 | Wire | |
Thermal conductivity | 20.0 °C | 150.0 - 180.0 W/(m·K) Show Material materials with Thermal conductivity of 150.0 - 180.0 W/(m·K) | H13 | EN 573-3 | Wire |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 21000000.0 - 25000000.0 S/m Show Material materials with Electrical conductivity of 21000000.0 - 25000000.0 S/m | H13 | EN 573-3 | Wire | |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m Show Material materials with Electrical resistivity of 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | H13 | EN 573-3, EN 1301 | Wire |
Copper | 2.2 - 3.0 % Show Material materials with Copper of 2.2 - 3.0 % | H13 | EN 573-3, EN 1301 | Wire |
Iron | 0.7 % Show Material materials with Iron of 0.7 % | H13 | EN 573-3 | Wire |
0.70 % Show Material materials with Iron of 0.70 % | H13 | EN 573-3, EN 1301 | Wire | |
Magnesium | 0.2 - 0.5 % Show Material materials with Magnesium of 0.2 - 0.5 % | H13 | EN 573-3, EN 1301 | Wire |
Manganese | 0.2 % Show Material materials with Manganese of 0.2 % | H13 | EN 573-3, EN 1301 | Wire |
Silicon | 0.8 % Show Material materials with Silicon of 0.8 % | H13 | EN 573-3, EN 1301 | Wire |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H13 | EN 573-3, EN 1301 | Wire |
Technological properties
| Property | ||
|---|---|---|
| Brazing | hard brazing (with flux/ without flux): sufficient / sufficient | |
| Corrosion properties | Seawater: poor, weathering: poor | |
| Workability | Moderate Workability | |