AA 2014 is an alloy with strength, machinability and welding capabilities, Aluminum Alloy AA 2014 is an excellent option. It is a precipitation hardening alloy that maintains strength after heat treatment.

Related Standards

Equivalent Materials

This material data has been provided by AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.8 g/cm³

Show Material materials with Density of 2.8 g/cm³

T451

AA Standards, ASTM B209, ASTM B211

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

140.0 MPa

Show Material materials with Bending Fatigue Strength of 140.0 MPa

T451

AA Standards

Unlock all property charts

Elastic modulus

73.0 GPa

Show Material materials with Elastic modulus of 73.0 GPa

T451

AA Standards, ASTM B209, ASTM B211

Unlock all property charts

Elongation A100

23.0 °C

7 - 18 %

Show Material materials with Elongation A100 of 7 - 18 %

Elongation A50

23.0 °C

14 - 16 %

Show Material materials with Elongation A50 of 14 - 16 %

Hardness, Brinell

105.0 [-]

Show Material materials with Hardness, Brinell of 105.0 [-]

T451

AA Standards

Unlock all property charts

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 2000 Series Aluminium

Unlock all property charts

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 2000 Series Aluminium

Unlock all property charts

Shear modulus

26.0 - 27.5 GPa

Show Material materials with Shear modulus of 26.0 - 27.5 GPa

Typical for Wrought 2000 Series Aluminium

Unlock all property charts

Tensile strength

425.0 MPa

Show Material materials with Tensile strength of 425.0 MPa

T451

AA Standards

395.0 MPa

Show Material materials with Tensile strength of 395.0 MPa

T451

AA Standards, ASTM B209

400.0 MPa

Show Material materials with Tensile strength of 400.0 MPa

T451

AA Standards, ASTM B209

380.0 MPa

Show Material materials with Tensile strength of 380.0 MPa

T451

AA Standards, ASTM B211

Unlock all property charts

Yield strength Rp0.2

23.0 °C

220 - 290 MPa

Show Material materials with Yield strength Rp0.2 of 220 - 290 MPa

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

100 °C, 20 °C

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T451

AA Standards, ASTM B209, ASTM B211

Unlock all property charts

Melting point

505.0 - 635.0 °C

Show Material materials with Melting point of 505.0 - 635.0 °C

T451

AA Standards, ASTM B209, ASTM B211

Specific heat capacity

816.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 816.0 - 963.0 J/(kg·K)

Typical for Wrought 2000 Series Aluminium

Unlock all property charts

Thermal conductivity

134.0 - 193.0 W/(m·K)

Show Material materials with Thermal conductivity of 134.0 - 193.0 W/(m·K)

T451

AA Standards, ASTM B209, ASTM B211

Unlock all property charts

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

20000000.0 - 29000000.0 S/m

Show Material materials with Electrical conductivity of 20000000.0 - 29000000.0 S/m

T451

AA Standards, ASTM B209, ASTM B211

Unlock all property charts

Electrical resistivity

3.45e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 3.45e-08 - 5e-08 Ω·m

T451

AA Standards, ASTM B209, ASTM B211

Unlock all property charts

Chemical properties

PropertyValueConditionRelated Standards

Chromium

0.1 %

Show Material materials with Chromium of 0.1 %

T451

AA Standards, ASTM B209, ASTM B211

Copper

3.9 - 5.0 %

Show Material materials with Copper of 3.9 - 5.0 %

T451

AA Standards, ASTM B209, ASTM B211

Iron

0.70 %

Show Material materials with Iron of 0.70 %

T451

AA Standards, ASTM B209, ASTM B211

Magnesium

0.2 - 0.8 %

Show Material materials with Magnesium of 0.2 - 0.8 %

T451

AA Standards, ASTM B209, ASTM B211

Manganese

0.4 - 1.2 %

Show Material materials with Manganese of 0.4 - 1.2 %

T451

AA Standards, ASTM B209, ASTM B211

Other

each 0.05, total 0.15, Rest Al

Silicon

0.5 - 1.2 %

Show Material materials with Silicon of 0.5 - 1.2 %

T451

AA Standards, ASTM B209, ASTM B211

Titanium

0.15 %

Show Material materials with Titanium of 0.15 %

T451

AA Standards, ASTM B209, ASTM B211

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

T451

AA Standards, ASTM B209, ASTM B211

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected

General machinability

General: poor (O), good to acceptable

Workability

general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511)