Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.73 g/cm³ Show Material materials with Density of 2.73 g/cm³ | H19 | EN 573-3, EN 485, EN 683 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H19 | EN 573-3, EN 485, EN 683 | |
69.5 GPa Show Material materials with Elastic modulus of 69.5 GPa | H19 | EN 573-3, EN 485, EN 683 | ||
Hardness, Brinell | 65.0 [-] Show Material materials with Hardness, Brinell of 65.0 [-] | H19 | EN 573-3, EN 485 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Shear modulus | 26.1 GPa Show Material materials with Shear modulus of 26.1 GPa | H19 | EN 573-3, EN 485, EN 683 | |
Tensile strength | 210.0 MPa Show Material materials with Tensile strength of 210.0 MPa | H19 | EN 573-3, EN 485, EN 683 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | -50 °C | 2.1499999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1499999999999997e-05 1/K | H19 | EN 573-3, EN 485, EN 683 |
20 °C | 2.1499999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1499999999999997e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | |
20 °C | 2.3199999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | |
20 °C | 2.41e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | |
20 °C | 2.52e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.52e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | |
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | |
200 °C | 2.41e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | |
300 °C | 2.52e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.52e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | |
Melting point | 640.0 - 655.0 °C Show Material materials with Melting point of 640.0 - 655.0 °C | H19 | EN 573-3, EN 485, EN 683 | |
643.0 - 654.0 °C Show Material materials with Melting point of 643.0 - 654.0 °C | H19 | EN 573-3, EN 485, EN 683 | ||
Specific heat capacity | 893.0 J/(kg·K) Show Material materials with Specific heat capacity of 893.0 J/(kg·K) | H19 | EN 573-3, EN 485, EN 683 | |
Thermal conductivity | 159.0 - 193.0 W/(m·K) Show Material materials with Thermal conductivity of 159.0 - 193.0 W/(m·K) | H19 | EN 573-3, EN 485, EN 683 | |
160.0 - 200.0 W/(m·K) Show Material materials with Thermal conductivity of 160.0 - 200.0 W/(m·K) | H19 | EN 573-3, EN 485, EN 683 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 23000000.0 - 29000000.0 S/m Show Material materials with Electrical conductivity of 23000000.0 - 29000000.0 S/m | H19 | EN 573-3, EN 485, EN 683 |
24000000.0 - 29000000.0 S/m Show Material materials with Electrical conductivity of 24000000.0 - 29000000.0 S/m | H19 | EN 573-3, EN 485, EN 683 | |
Electrical resistivity | 3.45e-08 - 4.17e-08 Ω·m Show Material materials with Electrical resistivity of 3.45e-08 - 4.17e-08 Ω·m | H19 | EN 573-3, EN 485, EN 683 |
3.45e-08 - 4.35e-08 Ω·m Show Material materials with Electrical resistivity of 3.45e-08 - 4.35e-08 Ω·m | H19 | EN 573-3, EN 485, EN 683 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Copper | 0.05 - 0.2 % Show Material materials with Copper of 0.05 - 0.2 % | H19 | EN 573-3, EN 485, EN 683 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | H19 | EN 573-3, EN 485, EN 683 |
Manganese | 1.0 - 1.5 % Show Material materials with Manganese of 1.0 - 1.5 % | H19 | EN 573-3, EN 485, EN 683 |
Silicon | 0.6 % Show Material materials with Silicon of 0.6 % | H19 | EN 573-3, EN 485, EN 683 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H19 | EN 573-3, EN 485, EN 683 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: sufficient, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good | |
| Corrosion properties | Seawater: good, weathering: very good | |
| Workability | Bending / Spinning (cold): very good / very good, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) very good (O) / very good (H12) | |