Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.66 g/cm³ Show Material materials with Density of 2.66 g/cm³ | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.5 GPa Show Material materials with Elastic modulus of 70.5 GPa | O3 | EN 573-3, EN 1715-3, EN 1715-4 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.5 GPa Show Material materials with Shear modulus of 26.5 GPa | O3 | EN 573-3, EN 1715-3, EN 1715-4 | |
Tensile strength | 190.0 - 230.0 MPa Show Material materials with Tensile strength of 190.0 - 230.0 MPa | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | O3 | EN 573-3, EN 1715-3, EN 1715-4 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3899999999999998e-05 1/K | O3 | EN 573-3, EN 1715-3, EN 1715-4 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 610.0 - 640.0 °C Show Material materials with Melting point of 610.0 - 640.0 °C | O3 | EN 573-3, EN 1715-3, EN 1715-4 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 140.0 - 160.0 W/(m·K) Show Material materials with Thermal conductivity of 140.0 - 160.0 W/(m·K) | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 20000000.0 - 23000000.0 S/m Show Material materials with Electrical conductivity of 20000000.0 - 23000000.0 S/m | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Electrical resistivity | 4.35e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 4.35e-08 - 5e-08 Ω·m | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Copper | 0.1 % Show Material materials with Copper of 0.1 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Magnesium | 2.6 - 3.6 % Show Material materials with Magnesium of 2.6 - 3.6 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Manganese | 0.5 % Show Material materials with Manganese of 0.5 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: gut (EQ: sehr gut), Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor | |
| Corrosion properties | Seawater: very good to good, weathering: very good | |
| Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (H12) | |