DIN 1725-1 Grade 3.3525 H12

Want to keep this datasheet? Save it now in your required format

Description

The alloy AlMg2Mn0,3 has similar characteristics as the alloy AlMg1,8. The additive of Mn causes an increase of the heat resistance of the material apart from a strength increase with the products of extruding. The material is characterised by a good corrosion resistance. It is sea water steady and steady against saline atmosphere. With the Mg content the strength increases, the cold forming capacity decreases. The alloy is nature hard, i.e. that only by a cold forming shaping however by a purposeful heat treatment a strength increase cannot be attained. The splinter-giving workability and the weldability are improved with increasing Mg content. Application: For metal goods (including table-ware), in food industry (including commercial devices). For transport containers e.g. rolling barrels, in the packaging industry as cans as well as for describe (e.g. road signs).

Related Standards

Equivalent Materials

This material data has been provided by WIAM,AluKey.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density		2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³	H12	EN 573-3, EN 1592, EN 485, EN 754
	20.0 °C	2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³	H12	DIN 1725-1, EN 573-3, EN 573-4	Flat, Wire

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Bending angle 180°		2.0 °/t Show Material materials with Bending angle 180° of 2.0 °/t	H12	EN 573-3, EN 485
Bending angle 90°		1.0 °/t Show Material materials with Bending angle 90° of 1.0 °/t	H12	EN 573-3, EN 485
		1.5 °/t Show Material materials with Bending angle 90° of 1.5 °/t	H12	EN 573-3, EN 485
		2.5 °/t Show Material materials with Bending angle 90° of 2.5 °/t	H12	EN 573-3, EN 485
Elastic modulus		70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa	H12	EN 573-3, EN 1592, EN 485, EN 754
	20.0 °C	70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa	H12	DIN 1725-1, EN 573-3, EN 573-4	Flat, Wire
Elongation		3.0 % Show Material materials with Elongation of 3.0 %	H12	EN 573-3, EN 485		A50
		4.0 % Show Material materials with Elongation of 4.0 %	H12	EN 573-3, EN 485, EN 754		A50
		5.0 % Show Material materials with Elongation of 5.0 %	H12	EN 573-3, EN 754		A100
		5.0 % Show Material materials with Elongation of 5.0 %	H12	EN 573-3, EN 485		A50
		8.0 % Show Material materials with Elongation of 8.0 %	H12	EN 573-3, EN 1592		A100
		8.0 % Show Material materials with Elongation of 8.0 %	H12	EN 573-3, EN 485		A50
		10.0 % Show Material materials with Elongation of 10.0 %	H12	EN 573-3, EN 485		A100
		10.0 % Show Material materials with Elongation of 10.0 %	H12	EN 573-3, EN 485		A50
	20.0 °C	4.0 % Show Material materials with Elongation of 4.0 %	H12	DIN 1725-1, EN 573-3, EN 573-4	Wire	A100
	20.0 °C	7.0 % Show Material materials with Elongation of 7.0 %	H12	DIN 1725-1, EN 573-3, EN 573-4	Wire	A10
	20.0 °C	8.0 % Show Material materials with Elongation of 8.0 %	H12	DIN 1725-1, EN 573-3, EN 573-4	Flat	A10
	20.0 °C	10.0 % Show Material materials with Elongation of 10.0 %	H12	DIN 1725-1, EN 573-3, EN 573-4	Flat
Hardness, Brinell		58.0 [-] Show Material materials with Hardness, Brinell of 58.0 [-]	H12	EN 573-3, EN 485
	20.0 °C	50.0 [-] Show Material materials with Hardness, Brinell of 50.0 [-]	H12	DIN 1725-1, EN 573-3, EN 573-4	Wire
	20.0 °C	60.0 [-] Show Material materials with Hardness, Brinell of 60.0 [-]	H12	DIN 1725-1, EN 573-3, EN 573-4	Flat
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Poisson's ratio		0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-]				Typical for Wrought 5000 Series Aluminium
Shear modulus		26.3 GPa Show Material materials with Shear modulus of 26.3 GPa	H12	EN 573-3, EN 1592, EN 485, EN 754
	20.0 °C	26.5 GPa Show Material materials with Shear modulus of 26.5 GPa	H12	DIN 1725-1, EN 573-3, EN 573-4	Flat, Wire
Shear strength	20.0 °C	120.0 MPa Show Material materials with Shear strength of 120.0 MPa	H12	DIN 1725-1, EN 573-3, EN 573-4	Wire
Tensile strength		180.0 - 220.0 MPa Show Material materials with Tensile strength of 180.0 - 220.0 MPa	H12	EN 573-3, EN 754
		190.0 - 230.0 MPa Show Material materials with Tensile strength of 190.0 - 230.0 MPa	H12	EN 573-3, EN 485
		210.0 MPa Show Material materials with Tensile strength of 210.0 MPa	H12	EN 573-3, EN 1592
	20.0 °C	190.0 MPa Show Material materials with Tensile strength of 190.0 MPa	H12	DIN 1725-1, EN 573-3, EN 573-4	Wire
	20.0 °C	205.0 - 245.0 MPa Show Material materials with Tensile strength of 205.0 - 245.0 MPa	H12	DIN 1725-1, EN 573-3, EN 573-4	Flat

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion	20 °C	2.3699999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3699999999999997e-05 1/K	H12	EN 573-3, EN 1592, EN 485, EN 754
	100 °C	2.3699999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3699999999999997e-05 1/K	H12	EN 573-3, EN 1592, EN 485, EN 754
Max service temperature		150.0 °C Show Material materials with Max service temperature of 150.0 °C				Typical for Wrought 5000 Series Aluminium
Melting point		610.0 - 650.0 °C Show Material materials with Melting point of 610.0 - 650.0 °C	H12	EN 573-3, EN 1592, EN 485, EN 754
Specific heat capacity	20.0 °C	921.0 J/(kg·K) Show Material materials with Specific heat capacity of 921.0 J/(kg·K)	H12	DIN 1725-1, EN 573-3, EN 573-4	Flat, Wire
Thermal conductivity		140.0 - 160.0 W/(m·K) Show Material materials with Thermal conductivity of 140.0 - 160.0 W/(m·K)	H12	EN 573-3, EN 1592, EN 485, EN 754
	20.0 °C	167.0 W/(m·K) Show Material materials with Thermal conductivity of 167.0 W/(m·K)	H12	DIN 1725-1, EN 573-3, EN 573-4	Flat, Wire

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape
Electrical conductivity		25000000.0 - 30000000.0 S/m Show Material materials with Electrical conductivity of 25000000.0 - 30000000.0 S/m	H12	EN 573-3, EN 1592, EN 485, EN 754
	20.0 °C	26000000.0 S/m Show Material materials with Electrical conductivity of 26000000.0 S/m	H12	DIN 1725-1, EN 573-3, EN 573-4	Flat, Wire
Electrical resistivity		3.33e-08 - 4e-08 Ω·m Show Material materials with Electrical resistivity of 3.33e-08 - 4e-08 Ω·m	H12	EN 573-3, EN 1592, EN 485, EN 754

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.15 % Show Material materials with Chromium of 0.15 %	H12	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat, Wire
Copper	0.15 % Show Material materials with Copper of 0.15 %	H12	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat, Wire
Iron	0.5 % Show Material materials with Iron of 0.5 %	H12	DIN 1725-1, EN 573-3, EN 573-4	Flat, Wire
	0.50 % Show Material materials with Iron of 0.50 %	H12	EN 573-3, EN 1592, EN 485, EN 754
Magnesium	1.7 - 2.4 % Show Material materials with Magnesium of 1.7 - 2.4 %	H12	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat, Wire
Manganese	0.1 - 0.5 % Show Material materials with Manganese of 0.1 - 0.5 %	H12	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat, Wire
Silicon	0.4 % Show Material materials with Silicon of 0.4 %	H12	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat, Wire
Titanium	0.15 % Show Material materials with Titanium of 0.15 %	H12	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat, Wire
Zinc	0.15 % Show Material materials with Zinc of 0.15 %	H12	DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754	Flat, Wire

Technological properties

Property
Anodizing	decorative: sufficient, Protective: very good
Brazing	hard brazing (with flux/ without flux): sufficient / poor, friction soldering: good, soft brazing with flux: sufficient
Corrosion properties	Seawater: good, weathering: very good
Workability	Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / acceptable (H12)

Looking for suppliers of this material? Click to see 2 supplier of DIN 1725-1 Grade 3.3525 H12 on Matmatch