General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 115.0 MPa Show Material materials with Bending Fatigue Strength of 115.0 MPa | H34 | EN 573-3, EN 1592, EN 485, EN 754 | |
Bending angle 180° | 2.0 °/t Show Material materials with Bending angle 180° of 2.0 °/t | H34 | EN 573-3, EN 485 | |
Bending angle 90° | 0.5 °/t Show Material materials with Bending angle 90° of 0.5 °/t | H34 | EN 573-3, EN 485 | |
1.5 °/t Show Material materials with Bending angle 90° of 1.5 °/t | H34 | EN 573-3, EN 485 | ||
2.5 °/t Show Material materials with Bending angle 90° of 2.5 °/t | H34 | EN 573-3, EN 485 | ||
3.0 °/t Show Material materials with Bending angle 90° of 3.0 °/t | H34 | EN 573-3, EN 485 | ||
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H34 | EN 573-3, EN 1592, EN 485, EN 754 | |
Hardness, Brinell | 62.0 [-] Show Material materials with Hardness, Brinell of 62.0 [-] | H34 | EN 573-3, EN 485 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.3 GPa Show Material materials with Shear modulus of 26.3 GPa | H34 | EN 573-3, EN 1592, EN 485, EN 754 | |
Tensile strength | 200.0 - 240.0 MPa Show Material materials with Tensile strength of 200.0 - 240.0 MPa | H34 | EN 573-3, EN 754 | |
210.0 - 250.0 MPa Show Material materials with Tensile strength of 210.0 - 250.0 MPa | H34 | EN 573-3, EN 485 | ||
230.0 MPa Show Material materials with Tensile strength of 230.0 MPa | H34 | EN 573-3, EN 1592 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3699999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3699999999999997e-05 1/K | H34 | EN 573-3, EN 1592, EN 485, EN 754 | |
100 °C | 2.3699999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3699999999999997e-05 1/K | H34 | EN 573-3, EN 1592, EN 485, EN 754 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 610.0 - 650.0 °C Show Material materials with Melting point of 610.0 - 650.0 °C | H34 | EN 573-3, EN 1592, EN 485, EN 754 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 140.0 - 160.0 W/(m·K) Show Material materials with Thermal conductivity of 140.0 - 160.0 W/(m·K) | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 25000000.0 - 30000000.0 S/m Show Material materials with Electrical conductivity of 25000000.0 - 30000000.0 S/m | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Electrical resistivity | 3.33e-08 - 4e-08 Ω·m Show Material materials with Electrical resistivity of 3.33e-08 - 4e-08 Ω·m | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Chromium | 0.15 % Show Material materials with Chromium of 0.15 % | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Copper | 0.15 % Show Material materials with Copper of 0.15 % | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Magnesium | 1.7 - 2.4 % Show Material materials with Magnesium of 1.7 - 2.4 % | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Manganese | 0.1 - 0.5 % Show Material materials with Manganese of 0.1 - 0.5 % | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Zinc | 0.15 % Show Material materials with Zinc of 0.15 % | H34 | EN 573-3, EN 1592, EN 485, EN 754 |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: sufficient, Protective: very good | |
Brazing | hard brazing (with flux/ without flux): sufficient / poor, friction soldering: good, soft brazing with flux: sufficient | |
Corrosion properties | Seawater: good, weathering: very good | |
Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / acceptable (H12) |