Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending angle 180° | 0.5 °/t Show Material materials with Bending angle 180° of 0.5 °/t | H111 | EN 573-3, EN 485 | |
Bending angle 90° | 0.5 °/t Show Material materials with Bending angle 90° of 0.5 °/t | H111 | EN 573-3, EN 485 | |
1.0 °/t Show Material materials with Bending angle 90° of 1.0 °/t | H111 | EN 573-3, EN 485 | ||
2.0 °/t Show Material materials with Bending angle 90° of 2.0 °/t | H111 | EN 573-3, EN 485 | ||
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H111 | EN 573-3, EN 485, EN 754, EN 755 | |
Hardness, Brinell | 44.0 [-] Show Material materials with Hardness, Brinell of 44.0 [-] | H111 | EN 573-3, EN 485 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.3 GPa Show Material materials with Shear modulus of 26.3 GPa | H111 | EN 573-3, EN 485, EN 754, EN 755 | |
Tensile strength | 150.0 - 200.0 MPa Show Material materials with Tensile strength of 150.0 - 200.0 MPa | H111 | EN 573-3, EN 754 | |
160.0 - 200.0 MPa Show Material materials with Tensile strength of 160.0 - 200.0 MPa | H111 | EN 573-3, EN 485 | ||
160.0 - 220.0 MPa Show Material materials with Tensile strength of 160.0 - 220.0 MPa | H111 | EN 573-3, EN 755 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3699999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3699999999999997e-05 1/K | H111 | EN 573-3, EN 485, EN 754, EN 755 | |
100 °C | 2.3699999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3699999999999997e-05 1/K | H111 | EN 573-3, EN 485, EN 754, EN 755 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 610.0 - 650.0 °C Show Material materials with Melting point of 610.0 - 650.0 °C | H111 | EN 573-3, EN 485, EN 754, EN 755 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 140.0 - 160.0 W/(m·K) Show Material materials with Thermal conductivity of 140.0 - 160.0 W/(m·K) | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 25000000.0 - 30000000.0 S/m Show Material materials with Electrical conductivity of 25000000.0 - 30000000.0 S/m | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Electrical resistivity | 3.33e-08 - 4e-08 Ω·m Show Material materials with Electrical resistivity of 3.33e-08 - 4e-08 Ω·m | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.15 % Show Material materials with Chromium of 0.15 % | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Copper | 0.15 % Show Material materials with Copper of 0.15 % | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Magnesium | 1.7 - 2.4 % Show Material materials with Magnesium of 1.7 - 2.4 % | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Manganese | 0.1 - 0.5 % Show Material materials with Manganese of 0.1 - 0.5 % | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Zinc | 0.15 % Show Material materials with Zinc of 0.15 % | H111 | EN 573-3, EN 485, EN 754, EN 755 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: sufficient, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): sufficient / poor, friction soldering: good, soft brazing with flux: sufficient | |
| Corrosion properties | Seawater: good, weathering: very good | |
| Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / acceptable (H12) | |