General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | T62 | EN 573-3, EN 485, EN 603 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending angle 90° | 2.5 °/t Show Material materials with Bending angle 90° of 2.5 °/t | T62 | EN 573-3, EN 485 | |
3.5 °/t Show Material materials with Bending angle 90° of 3.5 °/t | T62 | EN 573-3, EN 485 | ||
4.5 °/t Show Material materials with Bending angle 90° of 4.5 °/t | T62 | EN 573-3, EN 485 | ||
6.0 °/t Show Material materials with Bending angle 90° of 6.0 °/t | T62 | EN 573-3, EN 485 | ||
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | T62 | EN 573-3, EN 485, EN 603 | |
Hardness, Brinell | 83.0 [-] Show Material materials with Hardness, Brinell of 83.0 [-] | T62 | EN 573-3, EN 485 | |
84.0 [-] Show Material materials with Hardness, Brinell of 84.0 [-] | T62 | EN 573-3, EN 485 | ||
89.0 [-] Show Material materials with Hardness, Brinell of 89.0 [-] | T62 | EN 573-3, EN 485 | ||
91.0 [-] Show Material materials with Hardness, Brinell of 91.0 [-] | T62 | EN 573-3, EN 485 | ||
94.0 [-] Show Material materials with Hardness, Brinell of 94.0 [-] | T62 | EN 573-3, EN 485 | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.4 GPa Show Material materials with Shear modulus of 26.4 GPa | T62 | EN 573-3, EN 485, EN 603 | |
Tensile strength | 255.0 MPa Show Material materials with Tensile strength of 255.0 MPa | T62 | EN 573-3, EN 485 | |
260.0 MPa Show Material materials with Tensile strength of 260.0 MPa | T62 | EN 573-3, EN 485 | ||
275.0 MPa Show Material materials with Tensile strength of 275.0 MPa | T62 | EN 573-3, EN 485 | ||
295.0 MPa Show Material materials with Tensile strength of 295.0 MPa | T62 | EN 573-3, EN 485 | ||
310.0 MPa Show Material materials with Tensile strength of 310.0 MPa | T62 | EN 573-3, EN 485, EN 603 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T62 | EN 573-3, EN 485, EN 603 |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T62 | EN 573-3, EN 485, EN 603 | |
Melting point | 585.0 - 650.0 °C Show Material materials with Melting point of 585.0 - 650.0 °C | T62 | EN 573-3, EN 485, EN 603 | |
Specific heat capacity | 896.0 J/(kg·K) Show Material materials with Specific heat capacity of 896.0 J/(kg·K) | T62 | EN 573-3, EN 485, EN 603 | |
Thermal conductivity | 170.0 - 220.0 W/(m·K) Show Material materials with Thermal conductivity of 170.0 - 220.0 W/(m·K) | T62 | EN 573-3, EN 485, EN 603 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 24000000.0 - 32000000.0 S/m Show Material materials with Electrical conductivity of 24000000.0 - 32000000.0 S/m | T62 | EN 573-3, EN 485, EN 603 |
Electrical resistivity | 3.13e-08 - 4.17e-08 Ω·m Show Material materials with Electrical resistivity of 3.13e-08 - 4.17e-08 Ω·m | T62 | EN 573-3, EN 485, EN 603 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Chromium | 0.25 % Show Material materials with Chromium of 0.25 % | T62 | EN 573-3, EN 485, EN 603 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | T62 | EN 573-3, EN 485, EN 603 |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | T62 | EN 573-3, EN 485, EN 603 |
Magnesium | 0.6 - 1.2 % Show Material materials with Magnesium of 0.6 - 1.2 % | T62 | EN 573-3, EN 485, EN 603 |
Manganese | 0.4 - 1.0 % Show Material materials with Manganese of 0.4 - 1.0 % | T62 | EN 573-3, EN 485, EN 603 |
Silicon | 0.7 - 1.3 % Show Material materials with Silicon of 0.7 - 1.3 % | T62 | EN 573-3, EN 485, EN 603 |
Titanium | 0.1 % Show Material materials with Titanium of 0.1 % | T62 | EN 573-3, EN 485, EN 603 |
Zinc | 0.2 % Show Material materials with Zinc of 0.2 % | T62 | EN 573-3, EN 485, EN 603 |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: acceptable, Protective: very good | |
Brazing | hard brazing (with flux/ without flux): good / sufficient, friction soldering: good, soft brazing with flux: acceptable | |
Corrosion properties | Seawater: good, weathering: very good | |
Workability | Bending / Spinning (cold): acceptable (T3, T4) / good (O), Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) good (O) / good (O) |