Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ | H13 | EN 573-3, EN 1301 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H13 | EN 573-3, EN 1301 | |
70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H13 | EN 573-3, EN 1301 | ||
Elongation | 4.0 % Show Material materials with Elongation of 4.0 % | H13 | EN 573-3, EN 1301 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.3 GPa Show Material materials with Shear modulus of 26.3 GPa | H13 | EN 573-3, EN 1301 | |
Tensile strength | 150.0 - 210.0 MPa Show Material materials with Tensile strength of 150.0 - 210.0 MPa | H13 | EN 573-3, EN 1301 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | H13 | EN 573-3, EN 1301 | |
20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H13 | EN 573-3, EN 1301 | ||
100 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | H13 | EN 573-3, EN 1301 | ||
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H13 | EN 573-3, EN 1301 | ||
Melting point | 580.0 - 640.0 °C Show Material materials with Melting point of 580.0 - 640.0 °C | H13 | EN 573-3, EN 1301 | ||
580.0 - 650.0 °C Show Material materials with Melting point of 580.0 - 650.0 °C | H13 | EN 573-3, EN 1301 | |||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Thermal conductivity | 155.0 - 180.0 W/(m·K) Show Material materials with Thermal conductivity of 155.0 - 180.0 W/(m·K) | H13 | EN 573-3, EN 1301 | ||
170.0 - 200.0 W/(m·K) Show Material materials with Thermal conductivity of 170.0 - 200.0 W/(m·K) | H13 | EN 573-3, EN 1301 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 22000000.0 - 30000000.0 S/m Show Material materials with Electrical conductivity of 22000000.0 - 30000000.0 S/m | H13 | EN 573-3, EN 1301 |
23000000.0 - 27000000.0 S/m Show Material materials with Electrical conductivity of 23000000.0 - 27000000.0 S/m | H13 | EN 573-3, EN 1301 | |
Electrical resistivity | 3.33e-08 - 4.55e-08 Ω·m Show Material materials with Electrical resistivity of 3.33e-08 - 4.55e-08 Ω·m | H13 | EN 573-3, EN 1301 |
3.7e-08 - 4.35e-08 Ω·m Show Material materials with Electrical resistivity of 3.7e-08 - 4.35e-08 Ω·m | H13 | EN 573-3, EN 1301 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.04 - 0.35 % Show Material materials with Chromium of 0.04 - 0.35 % | H13 | EN 573-3, EN 1301 |
Copper | 0.15 - 0.4 % Show Material materials with Copper of 0.15 - 0.4 % | H13 | EN 573-3, EN 1301 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | H13 | EN 573-3, EN 1301 |
Magnesium | 0.8 - 1.2 % Show Material materials with Magnesium of 0.8 - 1.2 % | H13 | EN 573-3, EN 1301 |
Manganese | 0.15 % Show Material materials with Manganese of 0.15 % | H13 | EN 573-3, EN 1301 |
Silicon | 0.4 - 0.8 % Show Material materials with Silicon of 0.4 - 0.8 % | H13 | EN 573-3, EN 1301 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | H13 | EN 573-3, EN 1301 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H13 | EN 573-3, EN 1301 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): good / sufficient, friction soldering: good, soft brazing with flux: acceptable | |
| Corrosion properties | Seawater: good to acceptable, weathering: good | |
| Workability | Bending / Spinning (cold): acceptable (T3, T4) / good (O), Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) good (O) / good (O) | |