General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | T732 | EN 573-3, EN 603 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 72.0 GPa Show Material materials with Elastic modulus of 72.0 GPa | T732 | EN 573-3, EN 603 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||
Shear modulus | 27.1 GPa Show Material materials with Shear modulus of 27.1 GPa | T732 | EN 573-3, EN 603 | |
Tensile strength | 455.0 MPa Show Material materials with Tensile strength of 455.0 MPa | T732 | EN 573-3, EN 603 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | -50 °C | 2.16e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.16e-05 1/K | T732 | EN 573-3, EN 603 |
20 °C | 2.16e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.16e-05 1/K | T732 | EN 573-3, EN 603 | |
20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T732 | EN 573-3, EN 603 | |
20 °C | 2.43e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.43e-05 1/K | T732 | EN 573-3, EN 603 | |
20 °C | 2.52e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.52e-05 1/K | T732 | EN 573-3, EN 603 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3399999999999996e-05 1/K | T732 | EN 573-3, EN 603 | |
200 °C | 2.43e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.43e-05 1/K | T732 | EN 573-3, EN 603 | |
300 °C | 2.52e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.52e-05 1/K | T732 | EN 573-3, EN 603 | |
Melting point | 480.0 - 640.0 °C Show Material materials with Melting point of 480.0 - 640.0 °C | T732 | EN 573-3, EN 603 | |
Specific heat capacity | 862.0 J/(kg·K) Show Material materials with Specific heat capacity of 862.0 J/(kg·K) | T732 | EN 573-3, EN 603 | |
Thermal conductivity | 130.0 - 160.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 - 160.0 W/(m·K) | T732 | EN 573-3, EN 603 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 19000000.0 - 23000000.0 S/m Show Material materials with Electrical conductivity of 19000000.0 - 23000000.0 S/m | T732 | EN 573-3, EN 603 |
Electrical resistivity | 4.35e-08 - 5.26e-08 Ω·m Show Material materials with Electrical resistivity of 4.35e-08 - 5.26e-08 Ω·m | T732 | EN 573-3, EN 603 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Chromium | 0.18 - 0.28 % Show Material materials with Chromium of 0.18 - 0.28 % | T732 | EN 573-3, EN 603 |
Copper | 1.2 - 2.0 % Show Material materials with Copper of 1.2 - 2.0 % | T732 | EN 573-3, EN 603 |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | T732 | EN 573-3, EN 603 |
Magnesium | 2.1 - 2.9 % Show Material materials with Magnesium of 2.1 - 2.9 % | T732 | EN 573-3, EN 603 |
Manganese | 0.3 % Show Material materials with Manganese of 0.3 % | T732 | EN 573-3, EN 603 |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | T732 | EN 573-3, EN 603 |
Titanium | 0.2 % Show Material materials with Titanium of 0.2 % | T732 | EN 573-3, EN 603 |
Zinc | 5.1 - 6.1 % Show Material materials with Zinc of 5.1 - 6.1 % | T732 | EN 573-3, EN 603 |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: not suitable, Protective: acceptable | |
Brazing | hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: not suitable, soft brazing with flux: not suitable | |
Corrosion properties | Seawater: sufficient to poor, weathering: sufficient to poor | |
Workability | Bending / Spinning (cold): sufficient (O) / not suitable, Impact extrusion (cold): not suitable, Deep drawing / upsetting (Condition) not suitable / not suitable |