General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ | H19 | EN 573-3, EN 485, EN 683 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H19 | EN 573-3, EN 485, EN 683 | |
Hardness, Brinell | 48.0 [-] Show Material materials with Hardness, Brinell of 48.0 [-] | H19 | EN 573-3, EN 485 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa | H19 | EN 573-3, EN 485, EN 683 | |
Tensile strength | 160.0 MPa Show Material materials with Tensile strength of 160.0 MPa | H19 | EN 573-3, EN 485 | |
170.0 MPa Show Material materials with Tensile strength of 170.0 MPa | H19 | EN 573-3, EN 683 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | -50 °C | 2.17e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.17e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | |
20 °C | 2.17e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.17e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | ||
20 °C | 2.35e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.35e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | ||
20 °C | 2.4399999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4399999999999997e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | ||
20 °C | 2.5399999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.5399999999999997e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | ||
100 °C | 2.35e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.35e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | ||
200 °C | 2.4399999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4399999999999997e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | ||
300 °C | 2.5399999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.5399999999999997e-05 1/K | H19 | EN 573-3, EN 485, EN 683 | ||
Melting point | 644.0 - 657.0 °C Show Material materials with Melting point of 644.0 - 657.0 °C | H19 | EN 573-3, EN 485, EN 683 | ||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 205.0 - 210.0 W/(m·K) Show Material materials with Thermal conductivity of 205.0 - 210.0 W/(m·K) | H19 | EN 573-3, EN 485, EN 683 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 33000000.0 - 34000000.0 S/m Show Material materials with Electrical conductivity of 33000000.0 - 34000000.0 S/m | H19 | EN 573-3, EN 485, EN 683 |
Electrical resistivity | 2.94e-08 - 3.03e-08 Ω·m Show Material materials with Electrical resistivity of 2.94e-08 - 3.03e-08 Ω·m | H19 | EN 573-3, EN 485, EN 683 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 99.0 % Show Material materials with Aluminium of 99.0 % | H19 | EN 573-3, EN 485, EN 683 |
Copper | 0.05 % Show Material materials with Copper of 0.05 % | H19 | EN 573-3, EN 485, EN 683 |
Magnesium | 0.05 % Show Material materials with Magnesium of 0.05 % | H19 | EN 573-3, EN 485, EN 683 |
Manganese | 0.05 % Show Material materials with Manganese of 0.05 % | H19 | EN 573-3, EN 485, EN 683 |
Titanium | 0.05 % Show Material materials with Titanium of 0.05 % | H19 | EN 573-3, EN 485, EN 683 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H19 | EN 573-3, EN 485, EN 683 |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: acceptable, Protective: very good | |
Brazing | hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good | |
Corrosion properties | Seawater: sufficient, weathering: acceptable | |
Workability | Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H12) / very good (H12) |