AA Standards Grade 2014 T652

Want to keep this datasheet? Save it now in your required format

Description

AA 2014 is an alloy with strength, machinability and welding capabilities, Aluminum Alloy AA 2014 is an excellent option. It is a precipitation hardening alloy that maintains strength after heat treatment.

Related Standards

Equivalent Materials

This material data has been provided by AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.8 g/cm³

Show Material materials with Density of 2.8 g/cm³

T652

AA Standards, ASTM B247

Mechanical

PropertyValueConditionRelated StandardsComment

Elastic modulus

73.0 GPa

Show Material materials with Elastic modulus of 73.0 GPa

T652

AA Standards, ASTM B247

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 2000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 2000 Series Aluminium

Shear modulus

26.0 - 27.5 GPa

Show Material materials with Shear modulus of 26.0 - 27.5 GPa

Typical for Wrought 2000 Series Aluminium

Tensile strength

425.0 MPa

Show Material materials with Tensile strength of 425.0 MPa

T652

AA Standards, ASTM B247

450.0 MPa

Show Material materials with Tensile strength of 450.0 MPa

T652

AA Standards, ASTM B247

415.0 MPa

Show Material materials with Tensile strength of 415.0 MPa

T652

AA Standards, ASTM B247

420.0 MPa

Show Material materials with Tensile strength of 420.0 MPa

T652

AA Standards, ASTM B247

400.0 MPa

Show Material materials with Tensile strength of 400.0 MPa

T652

AA Standards, ASTM B247

405.0 MPa

Show Material materials with Tensile strength of 405.0 MPa

T652

AA Standards, ASTM B247

440.0 MPa

Show Material materials with Tensile strength of 440.0 MPa

T652

AA Standards, ASTM B247

435.0 MPa

Show Material materials with Tensile strength of 435.0 MPa

T652

AA Standards, ASTM B247

395.0 MPa

Show Material materials with Tensile strength of 395.0 MPa

T652

AA Standards, ASTM B247

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

100 °C, 20 °C

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T652

AA Standards, ASTM B247

Melting point

505.0 - 635.0 °C

Show Material materials with Melting point of 505.0 - 635.0 °C

T652

AA Standards, ASTM B247

Specific heat capacity

816.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 816.0 - 963.0 J/(kg·K)

Typical for Wrought 2000 Series Aluminium

Thermal conductivity

134.0 - 193.0 W/(m·K)

Show Material materials with Thermal conductivity of 134.0 - 193.0 W/(m·K)

T652

AA Standards, ASTM B247

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

20000000.0 - 29000000.0 S/m

Show Material materials with Electrical conductivity of 20000000.0 - 29000000.0 S/m

T652

AA Standards, ASTM B247

Electrical resistivity

3.45e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 3.45e-08 - 5e-08 Ω·m

T652

AA Standards, ASTM B247

Chemical properties

PropertyValueConditionRelated Standards

Chromium

0.1 %

Show Material materials with Chromium of 0.1 %

T652

AA Standards, ASTM B247

Copper

3.9 - 5.0 %

Show Material materials with Copper of 3.9 - 5.0 %

T652

AA Standards, ASTM B247

Iron

0.70 %

Show Material materials with Iron of 0.70 %

T652

AA Standards, ASTM B247

Magnesium

0.2 - 0.8 %

Show Material materials with Magnesium of 0.2 - 0.8 %

T652

AA Standards, ASTM B247

Manganese

0.4 - 1.2 %

Show Material materials with Manganese of 0.4 - 1.2 %

T652

AA Standards, ASTM B247

Silicon

0.5 - 1.2 %

Show Material materials with Silicon of 0.5 - 1.2 %

T652

AA Standards, ASTM B247

Titanium

0.15 %

Show Material materials with Titanium of 0.15 %

T652

AA Standards, ASTM B247

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

T652

AA Standards, ASTM B247

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected

General machinability

General: poor (O), good to acceptable

Workability

general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511)