AA Standards Grade 2017 T4

Want to keep this datasheet? Save it now in your required format

Description

Aluminum AA 2017 is a heat treatable wrought alloy that offers decent strength, ductility, and good machinability. Aluminum AA 2017 offers more strength than Aluminum 2011, and has fair workability and corrosion resistance. As with many aluminum alloys, Aluminum AA 2017 should not be welded as it reduces the alloy’s corrosion resistance.

Related Standards

Equivalent Materials

This material data has been provided by AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.79 g/cm³

Show Material materials with Density of 2.79 g/cm³

T4

AA Standards, ASTM B211, ASTM B316

Mechanical

PropertyValueConditionRelated StandardsComment

Bending Fatigue Strength

125.0 MPa

Show Material materials with Bending Fatigue Strength of 125.0 MPa

T4

AA Standards

Elastic modulus

73.0 GPa

Show Material materials with Elastic modulus of 73.0 GPa

T4

AA Standards, ASTM B211, ASTM B316

Hardness, Brinell

105.0 [-]

Show Material materials with Hardness, Brinell of 105.0 [-]

T4

AA Standards

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 2000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 2000 Series Aluminium

Shear modulus

26.0 - 27.5 GPa

Show Material materials with Shear modulus of 26.0 - 27.5 GPa

Typical for Wrought 2000 Series Aluminium

Tensile strength

425.0 MPa

Show Material materials with Tensile strength of 425.0 MPa

T4

AA Standards

380.0 MPa

Show Material materials with Tensile strength of 380.0 MPa

T4

AA Standards, ASTM B211, ASTM B316

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

100 °C, 20 °C

2.36e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K

T4

AA Standards, ASTM B211, ASTM B316

Melting point

510.0 - 640.0 °C

Show Material materials with Melting point of 510.0 - 640.0 °C

T4

AA Standards, ASTM B211, ASTM B316

Specific heat capacity

816.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 816.0 - 963.0 J/(kg·K)

Typical for Wrought 2000 Series Aluminium

Thermal conductivity

134.0 - 193.0 W/(m·K)

Show Material materials with Thermal conductivity of 134.0 - 193.0 W/(m·K)

T4

AA Standards, ASTM B211, ASTM B316

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

20000000.0 - 29000000.0 S/m

Show Material materials with Electrical conductivity of 20000000.0 - 29000000.0 S/m

T4

AA Standards, ASTM B211, ASTM B316

Electrical resistivity

3.45e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 3.45e-08 - 5e-08 Ω·m

T4

AA Standards, ASTM B211, ASTM B316

Chemical properties

PropertyValueConditionRelated Standards

Chromium

0.1 %

Show Material materials with Chromium of 0.1 %

T4

AA Standards, ASTM B211, ASTM B316

Copper

3.5 - 4.5 %

Show Material materials with Copper of 3.5 - 4.5 %

T4

AA Standards, ASTM B211, ASTM B316

Iron

0.70 %

Show Material materials with Iron of 0.70 %

T4

AA Standards, ASTM B211, ASTM B316

Magnesium

0.4 - 0.8 %

Show Material materials with Magnesium of 0.4 - 0.8 %

T4

AA Standards, ASTM B211, ASTM B316

Manganese

0.4 - 1.0 %

Show Material materials with Manganese of 0.4 - 1.0 %

T4

AA Standards, ASTM B211, ASTM B316

Silicon

0.2 - 0.8 %

Show Material materials with Silicon of 0.2 - 0.8 %

T4

AA Standards, ASTM B211, ASTM B316

Titanium

0.15 %

Show Material materials with Titanium of 0.15 %

T4

AA Standards, ASTM B211, ASTM B316

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

T4

AA Standards, ASTM B211, ASTM B316

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected

General machinability

General: good to acceptable

Workability

general (condition): poor(T4, T451)