Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.705 g/cm³ Show Material materials with Density of 2.705 g/cm³ | H22 | AA Standards, ASTM B209 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H22 | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Tensile strength | 75.0 - 110.0 MPa Show Material materials with Tensile strength of 75.0 - 110.0 MPa | H22 | AA Standards, ASTM B209 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H22 | AA Standards, ASTM B209 | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H22 | AA Standards, ASTM B209 | ||
Melting point | 645.0 - 655.0 °C Show Material materials with Melting point of 645.0 - 655.0 °C | H22 | AA Standards, ASTM B209 | ||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 230.0 - 234.0 W/(m·K) Show Material materials with Thermal conductivity of 230.0 - 234.0 W/(m·K) | H22 | AA Standards, ASTM B209 | ||
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 35000000.0 - 36000000.0 S/m Show Material materials with Electrical conductivity of 35000000.0 - 36000000.0 S/m | H22 | AA Standards, ASTM B209 |
Electrical resistivity | 2.78e-08 - 2.86e-08 Ω·m Show Material materials with Electrical resistivity of 2.78e-08 - 2.86e-08 Ω·m | H22 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.6 % Show Material materials with Aluminium of 99.6 % | H22 | AA Standards, ASTM B209 |
Copper | 0.05 % Show Material materials with Copper of 0.05 % | H22 | AA Standards, ASTM B209 |
Iron | 0.35 % Show Material materials with Iron of 0.35 % | H22 | AA Standards, ASTM B209 |
Magnesium | 0.03 % Show Material materials with Magnesium of 0.03 % | H22 | AA Standards, ASTM B209 |
Manganese | 0.03 % Show Material materials with Manganese of 0.03 % | H22 | AA Standards, ASTM B209 |
Silicon | 0.25 % Show Material materials with Silicon of 0.25 % | H22 | AA Standards, ASTM B209 |
Titanium | 0.03 % Show Material materials with Titanium of 0.03 % | H22 | AA Standards, ASTM B209 |
Vanadium | 0.05 % Show Material materials with Vanadium of 0.05 % | H22 | AA Standards, ASTM B209 |
Zinc | 0.05 % Show Material materials with Zinc of 0.05 % | H22 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
| Workability | general (condition): good (O, H12, H14), acceptable (H16, H18) | |