Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.77 g/cm³ Show Material materials with Density of 2.77 g/cm³ | T62 | WL 3.1354 | Strip, Sheet, Plate |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Bending angle 180° | 4.0 °/t Show Material materials with Bending angle 180° of 4.0 °/t | T62 | WL 3.1354 | Strip, Sheet, Plate | |
Elastic modulus | 72.4 GPa Show Material materials with Elastic modulus of 72.4 GPa | T62 | WL 3.1354 | Strip, Sheet, Plate | |
Hardness, Brinell | 120.0 [-] Show Material materials with Hardness, Brinell of 120.0 [-] | T62 | WL 3.1354 | Strip, Sheet, Plate | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 27.6 GPa Show Material materials with Shear modulus of 27.6 GPa | T62 | WL 3.1354 | Strip, Sheet, Plate | |
Tensile strength | 415.0 MPa Show Material materials with Tensile strength of 415.0 MPa | T62 | WL 3.1354 | Strip, Sheet, Plate | |
435.0 MPa Show Material materials with Tensile strength of 435.0 MPa | T62 | WL 3.1354 | Strip, Sheet, Plate | ||
440.0 MPa Show Material materials with Tensile strength of 440.0 MPa | T62 | WL 3.1354 | Strip, Sheet, Plate |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.1499999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1499999999999997e-05 1/K | T62 | WL 3.1354 | Strip, Sheet, Plate | |
100 °C | 2.1499999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1499999999999997e-05 1/K | T62 | WL 3.1354 | Strip, Sheet, Plate | ||
Melting point | 500.0 - 640.0 °C Show Material materials with Melting point of 500.0 - 640.0 °C | T62 | WL 3.1354 | Strip, Sheet, Plate | ||
Specific heat capacity | 816.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium | ||||
Thermal conductivity | 109.0 - 160.0 W/(m·K) Show Material materials with Thermal conductivity of 109.0 - 160.0 W/(m·K) | T62 | WL 3.1354 | Strip, Sheet, Plate | ||
Electrical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Electrical conductivity | 15000000.0 - 23000000.0 S/m Show Material materials with Electrical conductivity of 15000000.0 - 23000000.0 S/m | T62 | WL 3.1354 | Strip, Sheet, Plate |
Electrical resistivity | 4.35e-08 - 6.67e-08 Ω·m Show Material materials with Electrical resistivity of 4.35e-08 - 6.67e-08 Ω·m | T62 | WL 3.1354 | Strip, Sheet, Plate |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T62 | WL 3.1354 | Strip, Sheet, Plate |
Copper | 3.8 - 4.9 % Show Material materials with Copper of 3.8 - 4.9 % | T62 | WL 3.1354 | Strip, Sheet, Plate |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | T62 | WL 3.1354 | Strip, Sheet, Plate |
Magnesium | 1.2 - 1.8 % Show Material materials with Magnesium of 1.2 - 1.8 % | T62 | WL 3.1354 | Strip, Sheet, Plate |
Manganese | 0.3 - 0.9 % Show Material materials with Manganese of 0.3 - 0.9 % | T62 | WL 3.1354 | Strip, Sheet, Plate |
Silicon | 0.5 % Show Material materials with Silicon of 0.5 % | T62 | WL 3.1354 | Strip, Sheet, Plate |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | T62 | WL 3.1354 | Strip, Sheet, Plate |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T62 | WL 3.1354 | Strip, Sheet, Plate |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |