Properties
General
| Property | Value | Temperature | Comment |
|---|---|---|---|
Density | 2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³ at 23.0 °C | 23.0 °C | Typical for Wrought 4000 Series Aluminium |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Bending angle 180° | 1 °/t Show Material materials with Bending angle 180° of 1 °/t at 23.0 °C | 23.0 °C | |
Bending angle 90° | 0.5 °/t Show Material materials with Bending angle 90° of 0.5 °/t at 23.0 °C | 23.0 °C | |
Elastic modulus | 69 - 71 GPa Show Material materials with Elastic modulus of 69 - 71 GPa at 23.0 °C | 23.0 °C | Typical for Wrought 4000 Series Aluminium |
Elongation A50 | 2 % Show Material materials with Elongation A50 of 2 % at 23.0 °C | 23.0 °C | |
Elongation A50, transverse | 2 % Show Material materials with Elongation A50, transverse of 2 % at 20.0 °C | 20.0 °C | |
Hardness, Brinell | 45 - 60 [-] Show Material materials with Hardness, Brinell of 45 - 60 [-] at 20.0 °C | 20.0 °C | |
45 - 60 [-] Show Material materials with Hardness, Brinell of 45 - 60 [-] at 23.0 °C | 23.0 °C | ||
Plane-Strain Fracture Toughnes | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C | 23.0 °C | Typical for Wrought 4000 Series Aluminium |
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C | 23.0 °C | Typical for Wrought 4000 Series Aluminium |
Shear modulus | 26 GPa Show Material materials with Shear modulus of 26 GPa at 23.0 °C | 23.0 °C | Typical for Wrought 4000 Series Aluminium |
Tensile strength | 150 - 190 MPa Show Material materials with Tensile strength of 150 - 190 MPa at 23.0 °C | 23.0 °C | |
Tensile strength, transverse | 150 - 190 MPa Show Material materials with Tensile strength, transverse of 150 - 190 MPa at 20.0 °C | 20.0 °C | |
Yield strength Rp0.2 | 120 MPa Show Material materials with Yield strength Rp0.2 of 120 MPa at 23.0 °C | 23.0 °C | |
Yield strength Rp0.2, transverse | 120 MPa Show Material materials with Yield strength Rp0.2, transverse of 120 MPa at 20.0 °C | 20.0 °C | |
Thermal
| Property | Value | Temperature | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 1.2E-5 - 2.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-5 - 2.2E-5 1/K at 23.0 °C | 23.0 °C | Typical for Wrought 4000 Series Aluminium |
Melting point | 520 - 630 °C Show Material materials with Melting point of 520 - 630 °C | Typical for Wrought 4000 Series Aluminium | |
Specific heat capacity | 864 J/(kg·K) Show Material materials with Specific heat capacity of 864 J/(kg·K) at 23.0 °C | 23.0 °C | Typical for Wrought 4000 Series Aluminium |
Thermal conductivity | 138 - 155 W/(m·K) Show Material materials with Thermal conductivity of 138 - 155 W/(m·K) at 23.0 °C | 23.0 °C | Typical for Wrought 4000 Series Aluminium |
Electrical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Electrical conductivity | 2.30E+7 - 3.00E+7 S/m Show Material materials with Electrical conductivity of 2.30E+7 - 3.00E+7 S/m at 23.0 °C | 23.0 °C | Typical for Wrought 4000 Series Aluminium |
Electrical resistivity | 3.8E-8 - 5E-8 Ω·m Show Material materials with Electrical resistivity of 3.8E-8 - 5E-8 Ω·m at 23.0 °C | 23.0 °C | Typical for Wrought 4000 Series Aluminium |
Chemical properties
| Property | ||
|---|---|---|
Copper | 0.1 - 0.5 % | |
Iron | 0.7 % | |
Magnesium | 0.1 - 0.5 % | |
Manganese | 0.6 - 1.2 % | |
Other | each 0.05, total 0.15, Rest Al | |
Silicon | 1.8 - 2.2 % | |
Zinc | 0.2 % |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |