CTF54A (cemented carbide)

Want to keep this datasheet? Save it now in your required format

Description

Tungsten hard material for wear protection

Ashby charts

See where CTF54A (cemented carbide) falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Binder

Cobalt binder

Density

ρ

12.95 g/cm³ at 23 °C

Grain structure

Fine grain size

Mechanical

Compressive strength

Rmc

3000 MPa at 23 °C

Show Cobalt Matrix Composite materials with Compressive strength of 3000 MPa at 23 °C

Elastic modulus

E

440 GPa at 23 °C

Show Cobalt Matrix Composite materials with Elastic modulus of 440 GPa at 23 °C

Hardness, Rockwell A

HRA

85 [-] at 23 °C

Show Cobalt Matrix Composite materials with Hardness, Rockwell A of 85 [-] at 23 °C

Hardness, Vickers, 10

HV 10

920 [-] at 23 °C

Show Cobalt Matrix Composite materials with Hardness, Vickers, 10 of 920 [-] at 23 °C

Plane-Strain Fracture Toughnes

KIC

22 MPa·√m at 23 °C

Show Cobalt Matrix Composite materials with Plane-Strain Fracture Toughnes of 22 MPa·√m at 23 °C

Tensile strength, transverse

Rm,trans

3200 MPa at 23 °C

Show Cobalt Matrix Composite materials with Tensile strength, transverse of 3200 MPa at 23 °C

Thermal

Coefficient of thermal expansion

α

6.9E-6 1/K at 23 °C

Thermal conductivity

λ

90 W/(m·K) at 23 °C

Chemical properties

Element

Weight %

Comment

W

-

WC balance

Co

27 %

as binder

Technological properties

Primary Phase

Secondary Phase

This material data has been provided by Ceratizit.