Properties
General
| Property | Temperature | Value | |
|---|---|---|---|
Density | 23.0 °C | 14.15 g/cm³ Show Supplier Material materials with Density of 14.15 g/cm³ | |
Grain structure | Fine (0,8µm - 1,3µm) | ||
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 543 GPa Show Supplier Material materials with Elastic modulus of 543 GPa | |
Hardness, Rockwell A | 23.0 °C | 89.5 [-] Show Supplier Material materials with Hardness, Rockwell A of 89.5 [-] | |
Hardness, Vickers, 10 | 23.0 °C | 1310 [-] Show Supplier Material materials with Hardness, Vickers, 10 of 1310 [-] | EN ISO 6507-1 |
Hardness, Vickers, 30 | 23.0 °C | 1300 [-] Show Supplier Material materials with Hardness, Vickers, 30 of 1300 [-] | EN ISO 6507-1 |
Plane-Strain Fracture Toughnes | 23.0 °C | 15 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 15 MPa·√m | ISO 28079 |
Poisson's ratio | 23.0 °C | 0.22 [-] Show Supplier Material materials with Poisson's ratio of 0.22 [-] | |
Tensile strength, transverse | 23.0 °C | 3500 MPa Show Supplier Material materials with Tensile strength, transverse of 3500 MPa | DIN EN ISO 7438 |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.45E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.45E-6 1/K |
Specific heat capacity | 23.0 °C | 0.2 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 0.2 J/(kg·K) |
Thermal conductivity | 23.0 °C | 98 W/(m·K) Show Supplier Material materials with Thermal conductivity of 98 W/(m·K) |
Thermal diffusivity | 23.0 °C | 34.4 mm²/s Show Supplier Material materials with Thermal diffusivity of 34.4 mm²/s |
Chemical properties
Technological properties
| Property |
|---|