Properties
General
| Property | Temperature | Value | |
|---|---|---|---|
Density | 23.0 °C | 14.8 g/cm³ Show Supplier Material materials with Density of 14.8 g/cm³ | |
Grain structure | Submicron (0,5µm - 0,8µm) | ||
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 624 GPa Show Supplier Material materials with Elastic modulus of 624 GPa | |
Hardness, Rockwell A | 23.0 °C | 93.2 [-] Show Supplier Material materials with Hardness, Rockwell A of 93.2 [-] | |
Hardness, Vickers, 10 | 23.0 °C | 1850 [-] Show Supplier Material materials with Hardness, Vickers, 10 of 1850 [-] | EN ISO 6507-1 |
Hardness, Vickers, 30 | 23.0 °C | 1820 [-] Show Supplier Material materials with Hardness, Vickers, 30 of 1820 [-] | EN ISO 6507-1 |
Plane-Strain Fracture Toughnes | 23.0 °C | 9.3 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 9.3 MPa·√m | ISO 28079 |
Poisson's ratio | 23.0 °C | 0.21 [-] Show Supplier Material materials with Poisson's ratio of 0.21 [-] | |
Tensile strength, transverse | 23.0 °C | 3600 MPa Show Supplier Material materials with Tensile strength, transverse of 3600 MPa | DIN EN ISO 7438 |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 4.8E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4.8E-6 1/K |
Specific heat capacity | 23.0 °C | 0.2 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 0.2 J/(kg·K) |
Thermal conductivity | 23.0 °C | 73 W/(m·K) Show Supplier Material materials with Thermal conductivity of 73 W/(m·K) |
Thermal diffusivity | 23.0 °C | 24.4 mm²/s Show Supplier Material materials with Thermal diffusivity of 24.4 mm²/s |
Chemical properties
Technological properties
| Property |
|---|