General
Property | Temperature | Value | |
---|---|---|---|
Density | 23.0 °C | 14.55 g/cm³ Show Supplier Material materials with Density of 14.55 g/cm³ | |
Grain structure | Submicron (0,5µm - 0,8µm) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 586 GPa Show Supplier Material materials with Elastic modulus of 586 GPa | |
Hardness, Rockwell A | 23.0 °C | 91.8 [-] Show Supplier Material materials with Hardness, Rockwell A of 91.8 [-] | |
Hardness, Vickers, 10 | 23.0 °C | 1610 [-] Show Supplier Material materials with Hardness, Vickers, 10 of 1610 [-] | EN ISO 6507-1 |
Hardness, Vickers, 30 | 23.0 °C | 1590 [-] Show Supplier Material materials with Hardness, Vickers, 30 of 1590 [-] | EN ISO 6507-1 |
Plane-Strain Fracture Toughnes | 23.0 °C | 10.7 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 10.7 MPa·√m | ISO 28079 |
Poisson's ratio | 23.0 °C | 0.21 [-] Show Supplier Material materials with Poisson's ratio of 0.21 [-] | |
Tensile strength, transverse | 23.0 °C | 3650 MPa Show Supplier Material materials with Tensile strength, transverse of 3650 MPa | DIN EN ISO 7438 |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.1E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.1E-6 1/K |
Specific heat capacity | 23.0 °C | 0.21 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 0.21 J/(kg·K) |
Thermal conductivity | 23.0 °C | 74 W/(m·K) Show Supplier Material materials with Thermal conductivity of 74 W/(m·K) |
Thermal diffusivity | 23.0 °C | 24.7 mm²/s Show Supplier Material materials with Thermal diffusivity of 24.7 mm²/s |
Chemical properties
Technological properties
Property |
---|