General
Property | Temperature | Value | |
---|---|---|---|
Density | 23.0 °C | 14.1 g/cm³ Show Supplier Material materials with Density of 14.1 g/cm³ | |
Grain structure | Ultrafine (0,2µm - 0,5µm) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 549 GPa Show Supplier Material materials with Elastic modulus of 549 GPa | |
Hardness, Rockwell A | 23.0 °C | 92.7 [-] Show Supplier Material materials with Hardness, Rockwell A of 92.7 [-] | |
Hardness, Vickers, 10 | 23.0 °C | 1760 [-] Show Supplier Material materials with Hardness, Vickers, 10 of 1760 [-] | EN ISO 6507-1 |
Hardness, Vickers, 30 | 23.0 °C | 1730 [-] Show Supplier Material materials with Hardness, Vickers, 30 of 1730 [-] | EN ISO 6507-1 |
Plane-Strain Fracture Toughnes | 23.0 °C | 9.8 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 9.8 MPa·√m | ISO 28079 |
Poisson's ratio | 23.0 °C | 0.22 [-] Show Supplier Material materials with Poisson's ratio of 0.22 [-] | |
Tensile strength, transverse | 23.0 °C | 4600 MPa Show Supplier Material materials with Tensile strength, transverse of 4600 MPa | DIN EN ISO 7438 |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.4E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5.4E-6 1/K |
Specific heat capacity | 23.0 °C | 0.21 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 0.21 J/(kg·K) |
Thermal conductivity | 23.0 °C | 51 W/(m·K) Show Supplier Material materials with Thermal conductivity of 51 W/(m·K) |
Thermal diffusivity | 23.0 °C | 17.6 mm²/s Show Supplier Material materials with Thermal diffusivity of 17.6 mm²/s |
Chemical properties
Technological properties
Property |
---|