General
Property | Value | Condition | Testing Standard |
---|---|---|---|
Density | 1.48 g/cm³ Show Supplier Material materials with Density of 1.48 g/cm³ | dry | ISO 1183 |
Moisture absorption | 2.3 % Show Supplier Material materials with Moisture absorption of 2.3 % | dry | Sim. to ISO 62 |
Water absorption | 5.9 % Show Supplier Material materials with Water absorption of 5.9 % | dry | Sim. to ISO 62 |
Mechanical
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Elastic modulus | -40 °C | 14.5 GPa Show Supplier Material materials with Elastic modulus of 14.5 GPa | dry | ISO 527-1/-2 |
7 GPa Show Supplier Material materials with Elastic modulus of 7 GPa | conditioned | ISO 527-1/-2 | ||
13.5 GPa Show Supplier Material materials with Elastic modulus of 13.5 GPa | dry | ISO 527-1/-2 | ||
120 °C | 5.4 GPa Show Supplier Material materials with Elastic modulus of 5.4 GPa | dry | ISO 527-1/-2 | |
160 °C | 5 GPa Show Supplier Material materials with Elastic modulus of 5 GPa | dry | ISO 527-1/-2 | |
180 °C | 4.5 GPa Show Supplier Material materials with Elastic modulus of 4.5 GPa | dry | ISO 527-1/-2 | |
200 °C | 4 GPa Show Supplier Material materials with Elastic modulus of 4 GPa | dry | ISO 527-1/-2 | |
210 °C | 3.5 GPa Show Supplier Material materials with Elastic modulus of 3.5 GPa | dry | ISO 527-1/-2 | |
Elongation | -40 °C | 3 % Show Supplier Material materials with Elongation of 3 % | dry | ISO 527-1/-2 |
3 % Show Supplier Material materials with Elongation of 3 % | dry | ISO 527-1/-2 | ||
5.5 % Show Supplier Material materials with Elongation of 5.5 % | conditioned | ISO 527-1/-2 | ||
120 °C | 7 % Show Supplier Material materials with Elongation of 7 % | dry | ISO 527-1/-2 | |
160 °C | 8 % Show Supplier Material materials with Elongation of 8 % | dry | ISO 527-1/-2 | |
180 °C | 8.5 % Show Supplier Material materials with Elongation of 8.5 % | dry | ISO 527-1/-2 | |
200 °C | 9 % Show Supplier Material materials with Elongation of 9 % | dry | ISO 527-1/-2 | |
210 °C | 0.01 % Show Supplier Material materials with Elongation of 0.01 % | dry | ISO 527-1/-2 | |
Flexural modulus | 7 GPa Show Supplier Material materials with Flexural modulus of 7 GPa | conditioned | ISO 178 | |
12 GPa Show Supplier Material materials with Flexural modulus of 12 GPa | dry | ISO 178 | ||
120 °C | 5.8 GPa Show Supplier Material materials with Flexural modulus of 5.8 GPa | dry | ISO 178 | |
160 °C | 5.5 GPa Show Supplier Material materials with Flexural modulus of 5.5 GPa | dry | ISO 178 | |
180 °C | 5 GPa Show Supplier Material materials with Flexural modulus of 5 GPa | dry | ISO 178 | |
200 °C | 4.5 GPa Show Supplier Material materials with Flexural modulus of 4.5 GPa | dry | ISO 178 | |
210 °C | 4 GPa Show Supplier Material materials with Flexural modulus of 4 GPa | dry | ISO 178 | |
Flexural yield strength | 170 MPa Show Supplier Material materials with Flexural yield strength of 170 MPa | conditioned | ISO 178 | |
330 MPa Show Supplier Material materials with Flexural yield strength of 330 MPa | dry | ISO 178 | ||
120 °C | 135 MPa Show Supplier Material materials with Flexural yield strength of 135 MPa | dry | ISO 178 | |
160 °C | 125 MPa Show Supplier Material materials with Flexural yield strength of 125 MPa | dry | ISO 178 | |
180 °C | 100 MPa Show Supplier Material materials with Flexural yield strength of 100 MPa | dry | ISO 178 | |
200 °C | 85 MPa Show Supplier Material materials with Flexural yield strength of 85 MPa | dry | ISO 178 | |
210 °C | 70 MPa Show Supplier Material materials with Flexural yield strength of 70 MPa | dry | ISO 178 | |
Impact strength, Charpy notched | -30 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m² | dry, conditioned | ISO 179/1eA |
23 °C | 13 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m² | dry | ISO 179/1eA | |
23 °C | 20 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 20 kJ/m² | conditioned | ISO 179/1eA | |
Impact strength, Charpy unnotched | -30 °C | 65 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 65 kJ/m² | dry | ISO 179/1eU |
-30 °C | 75 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 75 kJ/m² | conditioned | ISO 179/1eU | |
23 °C | 80 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | dry | ISO 179/1eU | |
23 °C | 90 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 90 kJ/m² | conditioned | ISO 179/1eU | |
Tensile strength | -40 °C | 280 MPa Show Supplier Material materials with Tensile strength of 280 MPa | dry | ISO 527-1/-2 |
130 MPa Show Supplier Material materials with Tensile strength of 130 MPa | conditioned | ISO 527-1/-2 | ||
215 MPa Show Supplier Material materials with Tensile strength of 215 MPa | dry | ISO 527-1/-2 | ||
120 °C | 105 MPa Show Supplier Material materials with Tensile strength of 105 MPa | dry | ISO 527-1/-2 | |
160 °C | 85 MPa Show Supplier Material materials with Tensile strength of 85 MPa | dry | ISO 527-1/-2 | |
180 °C | 75 MPa Show Supplier Material materials with Tensile strength of 75 MPa | dry | ISO 527-1/-2 | |
200 °C | 60 MPa Show Supplier Material materials with Tensile strength of 60 MPa | dry | ISO 527-1/-2 | |
210 °C | 50 MPa Show Supplier Material materials with Tensile strength of 50 MPa | dry | ISO 527-1/-2 |
Thermal
Property | Value | Condition | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|
Glass transition temperature | 68 °C Show Supplier Material materials with Glass transition temperature of 68 °C | dry | ASTM D5026/D7028 | DMTA (tan d) | |
70 °C Show Supplier Material materials with Glass transition temperature of 70 °C | dry | ISO 11357-1/-2 | 10°C/min | ||
Heat deflection temperature | 263 °C Show Supplier Material materials with Heat deflection temperature of 263 °C | dry | ISO 75-1/-2 | 2 MPa | |
275 °C Show Supplier Material materials with Heat deflection temperature of 275 °C | dry | ISO 75-1/-2 | 0.45 MPa | ||
Melting point | 285 °C Show Supplier Material materials with Melting point of 285 °C | dry | ISO 11357-1/-3 | 10°C/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Air inlet manifolds, Integrated Air Inlet Manifolds (up to 230°C), Resonators and ByPass Valves, Charge Air Cooler Caps, EGR mixing tube | |
Fillers | 40% Glass Fiber |