General
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Density | 1.62 g/cm³ Show Supplier Material materials with Density of 1.62 g/cm³ | dry | ISO 1183 | |
Moisture absorption | 2.2 % Show Supplier Material materials with Moisture absorption of 2.2 % | dry | Sim. to ISO 62 | |
Water absorption | 2.2 % Show Supplier Material materials with Water absorption of 2.2 % | dry | ISO 62 | at 23°C after 24h |
5.4 % Show Supplier Material materials with Water absorption of 5.4 % | dry | Sim. to ISO 62 |
Mechanical
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Elastic modulus | 8 GPa Show Supplier Material materials with Elastic modulus of 8 GPa | conditioned | ISO 527-1/-2 | |
17 GPa Show Supplier Material materials with Elastic modulus of 17 GPa | dry | ISO 527-1/-2 | ||
120 °C | 6.7 GPa Show Supplier Material materials with Elastic modulus of 6.7 GPa | dry | ISO 527-1/-2 | |
160 °C | 5.8 GPa Show Supplier Material materials with Elastic modulus of 5.8 GPa | dry | ISO 527-1/-2 | |
180 °C | 5.3 GPa Show Supplier Material materials with Elastic modulus of 5.3 GPa | dry | ISO 527-1/-2 | |
200 °C | 4.3 GPa Show Supplier Material materials with Elastic modulus of 4.3 GPa | dry | ISO 527-1/-2 | |
210 °C | 3.6 GPa Show Supplier Material materials with Elastic modulus of 3.6 GPa | dry | ISO 527-1/-2 | |
Elongation | 2.4 % Show Supplier Material materials with Elongation of 2.4 % | dry | ISO 527-1/-2 | |
6.3 % Show Supplier Material materials with Elongation of 6.3 % | conditioned | ISO 527-1/-2 | ||
120 °C | 7.5 % Show Supplier Material materials with Elongation of 7.5 % | dry | ISO 527-1/-2 | |
160 °C | 8.5 % Show Supplier Material materials with Elongation of 8.5 % | dry | ISO 527-1/-2 | |
180 °C | 9 % Show Supplier Material materials with Elongation of 9 % | dry | ISO 527-1/-2 | |
200 °C | 9.5 % Show Supplier Material materials with Elongation of 9.5 % | dry | ISO 527-1/-2 | |
210 °C | 0.01 % Show Supplier Material materials with Elongation of 0.01 % | dry | ISO 527-1/-2 | |
Flexural modulus | 8 GPa Show Supplier Material materials with Flexural modulus of 8 GPa | conditioned | ISO 178 | |
17 GPa Show Supplier Material materials with Flexural modulus of 17 GPa | dry | ISO 178 | ||
120 °C | 6.9 GPa Show Supplier Material materials with Flexural modulus of 6.9 GPa | dry | ISO 178 | |
160 °C | 6.1 GPa Show Supplier Material materials with Flexural modulus of 6.1 GPa | dry | ISO 178 | |
180 °C | 5.6 GPa Show Supplier Material materials with Flexural modulus of 5.6 GPa | dry | ISO 178 | |
200 °C | 4.5 GPa Show Supplier Material materials with Flexural modulus of 4.5 GPa | dry | ISO 178 | |
210 °C | 4.1 GPa Show Supplier Material materials with Flexural modulus of 4.1 GPa | dry | ISO 178 | |
Flexural yield strength | 205 MPa Show Supplier Material materials with Flexural yield strength of 205 MPa | conditioned | ISO 178 | |
370 MPa Show Supplier Material materials with Flexural yield strength of 370 MPa | dry | ISO 178 | ||
120 °C | 145 MPa Show Supplier Material materials with Flexural yield strength of 145 MPa | dry | ISO 178 | |
160 °C | 110 MPa Show Supplier Material materials with Flexural yield strength of 110 MPa | dry | ISO 178 | |
180 °C | 95 MPa Show Supplier Material materials with Flexural yield strength of 95 MPa | dry | ISO 178 | |
200 °C | 75 MPa Show Supplier Material materials with Flexural yield strength of 75 MPa | dry | ISO 178 | |
210 °C | 65 MPa Show Supplier Material materials with Flexural yield strength of 65 MPa | dry | ISO 178 | |
Impact strength, Charpy notched | -30 °C | 14.0 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14.0 kJ/m² | dry, conditioned | ISO 179/1eA |
23 °C | 17 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 17 kJ/m² | dry | ISO 179/1eA | |
23 °C | 30 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 30 kJ/m² | conditioned | ISO 179/1eA | |
Impact strength, Charpy unnotched | -30 °C | 80 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | dry | ISO 179/1eU |
-30 °C | 95 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 95 kJ/m² | conditioned | ISO 179/1eU | |
23 °C | 95 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 95 kJ/m² | dry | ISO 179/1eU | |
23 °C | 110 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 110 kJ/m² | conditioned | ISO 179/1eU | |
Tensile strength | 135 MPa Show Supplier Material materials with Tensile strength of 135 MPa | conditioned | ISO 527-1/-2 | |
240 MPa Show Supplier Material materials with Tensile strength of 240 MPa | dry | ISO 527-1/-2 | ||
120 °C | 110 MPa Show Supplier Material materials with Tensile strength of 110 MPa | dry | ISO 527-1/-2 | |
160 °C | 85 MPa Show Supplier Material materials with Tensile strength of 85 MPa | dry | ISO 527-1/-2 | |
180 °C | 75 MPa Show Supplier Material materials with Tensile strength of 75 MPa | dry | ISO 527-1/-2 | |
200 °C | 60 MPa Show Supplier Material materials with Tensile strength of 60 MPa | dry | ISO 527-1/-2 | |
210 °C | 55.0 MPa Show Supplier Material materials with Tensile strength of 55.0 MPa | dry | ISO 527-1/-2 |
Thermal
Property | Value | Condition | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 2.5e-07 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.5e-07 1/K | dry | ISO 11359-1/-2 | Parallel | |
4e-07 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4e-07 1/K | dry | ISO 11359-1/-2 | Normal | ||
Glass transition temperature | 75 °C Show Supplier Material materials with Glass transition temperature of 75 °C | dry | ISO 11357-1/-2 | 10°C/min | |
Heat deflection temperature | 260 °C Show Supplier Material materials with Heat deflection temperature of 260 °C | dry | ISO 75-1/-2 | 2 MPa | |
270 °C Show Supplier Material materials with Heat deflection temperature of 270 °C | dry | ISO 75-1/-2 | 0.45 MPa | ||
Melting point | 275 °C Show Supplier Material materials with Melting point of 275 °C | dry | ISO 11357-1/-3 | 10°C/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 50% Glass Fiber |