Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Density | 1.62 g/cm³ Show Supplier Material materials with Density of 1.62 g/cm³ | dry | ISO 1183 | |
Limiting oxygen index | 22 % Show Supplier Material materials with Limiting oxygen index of 22 % | dry | ISO 4589-1/-2 | |
Moisture absorption | 1.85 % Show Supplier Material materials with Moisture absorption of 1.85 % | dry | Sim. to ISO 62 | |
Water absorption | 1.9 % Show Supplier Material materials with Water absorption of 1.9 % | dry | ISO 62 | at 23°C after 24h |
6.75 % Show Supplier Material materials with Water absorption of 6.75 % | dry | Sim. to ISO 62 |
Mechanical
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Elastic modulus | 10 GPa Show Supplier Material materials with Elastic modulus of 10 GPa | conditioned | ISO 527-1/-2 | |
16 GPa Show Supplier Material materials with Elastic modulus of 16 GPa | dry | ISO 527-1/-2 | ||
120 °C | 8.5 GPa Show Supplier Material materials with Elastic modulus of 8.5 GPa | dry | ISO 527-1/-2 | |
160 °C | 7.2 GPa Show Supplier Material materials with Elastic modulus of 7.2 GPa | dry | ISO 527-1/-2 | |
180 °C | 6.6 GPa Show Supplier Material materials with Elastic modulus of 6.6 GPa | dry | ISO 527-1/-2 | |
200 °C | 6 GPa Show Supplier Material materials with Elastic modulus of 6 GPa | dry | ISO 527-1/-2 | |
Elongation | 2.7 % Show Supplier Material materials with Elongation of 2.7 % | dry | ISO 527-1/-2 | |
5 % Show Supplier Material materials with Elongation of 5 % | conditioned | ISO 527-1/-2 | ||
120 °C | 5 % Show Supplier Material materials with Elongation of 5 % | dry | ISO 527-1/-2 | |
160 °C | 5.5 % Show Supplier Material materials with Elongation of 5.5 % | dry | ISO 527-1/-2 | |
180 °C | 5.5 % Show Supplier Material materials with Elongation of 5.5 % | dry | ISO 527-1/-2 | |
200 °C | 6 % Show Supplier Material materials with Elongation of 6 % | dry | ISO 527-1/-2 | |
Flexural modulus | 9 GPa Show Supplier Material materials with Flexural modulus of 9 GPa | conditioned | ISO 178 | |
15 GPa Show Supplier Material materials with Flexural modulus of 15 GPa | dry | ISO 178 | ||
120 °C | 7.3 GPa Show Supplier Material materials with Flexural modulus of 7.3 GPa | dry | ISO 178 | |
160 °C | 6.5 GPa Show Supplier Material materials with Flexural modulus of 6.5 GPa | dry | ISO 178 | |
Flexural yield strength | 250 MPa Show Supplier Material materials with Flexural yield strength of 250 MPa | conditioned | ISO 178 | |
380 MPa Show Supplier Material materials with Flexural yield strength of 380 MPa | dry | ISO 178 | ||
120 °C | 180 MPa Show Supplier Material materials with Flexural yield strength of 180 MPa | dry | ISO 178 | |
160 °C | 150 MPa Show Supplier Material materials with Flexural yield strength of 150 MPa | dry | ISO 178 | |
Impact strength, Charpy notched | -30 °C | 14.0 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14.0 kJ/m² | dry, conditioned | ISO 179/1eA |
23 °C | 16 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 16 kJ/m² | dry | ISO 179/1eA | |
23 °C | 24 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 24 kJ/m² | conditioned | ISO 179/1eA | |
Impact strength, Charpy unnotched | -30 °C | 90 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 90 kJ/m² | dry | ISO 179/1eU |
-30 °C | 100 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | conditioned | ISO 179/1eU | |
23 °C | 100 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | dry | ISO 179/1eU | |
23 °C | 110 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 110 kJ/m² | conditioned | ISO 179/1eU | |
Tensile strength | 150 MPa Show Supplier Material materials with Tensile strength of 150 MPa | conditioned | ISO 527-1/-2 | |
250 MPa Show Supplier Material materials with Tensile strength of 250 MPa | dry | ISO 527-1/-2 | ||
120 °C | 140 MPa Show Supplier Material materials with Tensile strength of 140 MPa | dry | ISO 527-1/-2 | |
160 °C | 120 MPa Show Supplier Material materials with Tensile strength of 120 MPa | dry | ISO 527-1/-2 | |
180 °C | 110 MPa Show Supplier Material materials with Tensile strength of 110 MPa | dry | ISO 527-1/-2 | |
200 °C | 100 MPa Show Supplier Material materials with Tensile strength of 100 MPa | dry | ISO 527-1/-2 |
Thermal
Property | Value | Condition | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 2.5e-07 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.5e-07 1/K | dry | ISO 11359-1/-2 | Parallel | |
4e-07 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4e-07 1/K | dry | ISO 11359-1/-2 | Normal | ||
Glass transition temperature | 75 °C Show Supplier Material materials with Glass transition temperature of 75 °C | dry | ISO 11357-1/-2 | 10°C/min | |
Heat deflection temperature | 290 °C Show Supplier Material materials with Heat deflection temperature of 290 °C | dry | ISO 75-1/-2 | 2 MPa | |
290 °C Show Supplier Material materials with Heat deflection temperature of 290 °C | dry | ISO 75-1/-2 | 0.45 MPa | ||
Melting point | 295 °C Show Supplier Material materials with Melting point of 295 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Thermal diffusivity | 1.32e-07 mm²/s Show Supplier Material materials with Thermal diffusivity of 1.32e-07 mm²/s | dry | - | ||
Vicat softening temperature | 290 °C Show Supplier Material materials with Vicat softening temperature of 290 °C | dry | ISO 306 | 50°C/h 50N |
Electrical
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Comparative tracking index | 300 V Show Supplier Material materials with Comparative tracking index of 300 V | dry | IEC 60112 | |
Dielectric constant | 4 [-] Show Supplier Material materials with Dielectric constant of 4 [-] | dry | IEC 62631-2-1 | 1MHz |
4.3 [-] Show Supplier Material materials with Dielectric constant of 4.3 [-] | dry | IEC 62631-2-1 | 100Hz | |
4.7 [-] Show Supplier Material materials with Dielectric constant of 4.7 [-] | conditioned | IEC 62631-2-1 | 1MHz | |
16 [-] Show Supplier Material materials with Dielectric constant of 16 [-] | conditioned | IEC 62631-2-1 | 100Hz | |
Dielectric strength | 20 kV/mm Show Supplier Material materials with Dielectric strength of 20 kV/mm | conditioned | IEC 60243-1 | |
30 kV/mm Show Supplier Material materials with Dielectric strength of 30 kV/mm | dry | IEC 60243-1 | ||
Dissipation factor | 70 [-] Show Supplier Material materials with Dissipation factor of 70 [-] | dry | IEC 62631-2-1 | 100Hz |
200 [-] Show Supplier Material materials with Dissipation factor of 200 [-] | dry | IEC 62631-2-1 | 1MHz | |
1000 [-] Show Supplier Material materials with Dissipation factor of 1000 [-] | conditioned | IEC 62631-2-1 | 1MHz | |
6000 [-] Show Supplier Material materials with Dissipation factor of 6000 [-] | conditioned | IEC 62631-2-1 | 100Hz | |
Surface resistivity | 1e+13 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+13 Ω/sq | conditioned | IEC 62631-3-2 | |
Volume resistivity | 1e+08 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+08 Ω·cm | conditioned | IEC 62631-3-1 | |
1e+12 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+12 Ω·cm | dry | IEC 62631-3-1 |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Density of melt | 1490 g/cm³ Show Supplier Material materials with Density of melt of 1490 g/cm³ | dry | - | |
Shrinkage | 0.4 % Show Supplier Material materials with Shrinkage of 0.4 % | dry | Sim. to ISO 294-4 | Parallel |
0.9 % Show Supplier Material materials with Shrinkage of 0.9 % | dry | Sim. to ISO 294-4 | Normal | |
Specific heat capacity melt | 1970 J/(kg·K) Show Supplier Material materials with Specific heat capacity melt of 1970 J/(kg·K) | dry | - | |
Spiral flow length | 70 | dry | - | 1.0 mm 800 bar |
80 | dry | - | 1.0 mm 900 bar | |
90 | dry | - | 1.0 mm 1000 bar | |
Thermal conductivity of melt | 0.387 W/(m·K) Show Supplier Material materials with Thermal conductivity of melt of 0.387 W/(m·K) | dry | - | |
Viscosity number | 140 cm³/gr Show Supplier Material materials with Viscosity number of 140 cm³/gr | dry | ISO 307, 1157, 1628 |
Technological properties
Property | ||
---|---|---|
Certifications | Yellow Card Available | |
Fillers | 50% Glass Fiber |