General
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Density | 1.22 g/cm³ Show Supplier Material materials with Density of 1.22 g/cm³ | dry | ISO 1183 | |
Moisture absorption | 0.5 % Show Supplier Material materials with Moisture absorption of 0.5 % | dry | Sim. to ISO 62 | |
Water absorption | 2.2 % Show Supplier Material materials with Water absorption of 2.2 % | dry | ISO 62 | at 23°C after 24h |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 0.17 GPa Show Supplier Material materials with Elastic modulus of 0.17 GPa | dry | ISO 527-1/-2 | ||
Elongation | 150 % Show Supplier Material materials with Elongation of 150 % | dry | ISO 527-1/-2 | ||
640 % Show Supplier Material materials with Elongation of 640 % | dry | ISO 527-1/-2 | |||
Flexural modulus | 0.2 GPa Show Supplier Material materials with Flexural modulus of 0.2 GPa | dry | ISO 178 | ||
120 °C | 0.07 GPa Show Supplier Material materials with Flexural modulus of 0.07 GPa | dry | ISO 178 | ||
Hardness, Shore A | 94 [-] Show Supplier Material materials with Hardness, Shore A of 94 [-] | dry | ISO 868 | 3s | |
Hardness, Shore D | 50 [-] Show Supplier Material materials with Hardness, Shore D of 50 [-] | dry | ISO 868 | 3s | |
Impact strength, Charpy notched | -30 °C | 14.0 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14.0 kJ/m² | dry | ISO 179/1eA | |
Tear strength | 116 kN/m Show Supplier Material materials with Tear strength of 116 kN/m | dry | ISO 34-1; Method B | ||
121 kN/m Show Supplier Material materials with Tear strength of 121 kN/m | dry | ISO 34-1; Method B | |||
Tensile strength | 27 MPa Show Supplier Material materials with Tensile strength of 27 MPa | dry | ISO 527-1/-2 | ||
36 MPa Show Supplier Material materials with Tensile strength of 36 MPa | dry | ISO 527-1/-2 | Normal |
Thermal
Property | Value | Condition | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|
Glass transition temperature | -57.0 °C Show Supplier Material materials with Glass transition temperature of -57.0 °C | dry | ISO 11357-1/-2 | 10°C/min | |
Heat deflection temperature | 63 °C Show Supplier Material materials with Heat deflection temperature of 63 °C | dry | ISO 75-1/-2 | 0.45 MPa | |
Melting point | 202 °C Show Supplier Material materials with Melting point of 202 °C | dry | ISO 11357-1/-3 | 10°C/min |
Rheological Properties
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Melt volume-flow rate | 230 °C | 2 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 2 cm³/10min | dry | ISO 1133 | |
Shrinkage | 1.7 % Show Supplier Material materials with Shrinkage of 1.7 % | dry | ISO 294-4 | Parallel | |
1.8 % Show Supplier Material materials with Shrinkage of 1.8 % | dry | ISO 294-4 | Normal |
Technological properties
Property | ||
---|---|---|
Application areas | Clean Air Inlet Ducts, Cold Charged Air Ducts |