General
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Density | 1.43 g/cm³ Show Supplier Material materials with Density of 1.43 g/cm³ | dry | ISO 1183 | |
Moisture absorption | 2.5 % Show Supplier Material materials with Moisture absorption of 2.5 % | dry | Sim. to ISO 62 | |
Water absorption | 2.6 % Show Supplier Material materials with Water absorption of 2.6 % | dry | ISO 62 | at 23°C after 24h |
9 % Show Supplier Material materials with Water absorption of 9 % | dry | Sim. to ISO 62 |
Mechanical
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Elastic modulus | -40 °C | 10 GPa Show Supplier Material materials with Elastic modulus of 10 GPa | dry | ISO 527-1/-2 |
Elongation | -40 °C | 3.2 % Show Supplier Material materials with Elongation of 3.2 % | dry | ISO 527-1/-2 |
3.5 % Show Supplier Material materials with Elongation of 3.5 % | dry | ISO 527-1/-2 | ||
7 % Show Supplier Material materials with Elongation of 7 % | conditioned | ISO 527-1/-2 | ||
120 °C | 8.4 % Show Supplier Material materials with Elongation of 8.4 % | dry | ISO 527-1/-2 | |
160 °C | 8.9 % Show Supplier Material materials with Elongation of 8.9 % | dry | ISO 527-1/-2 | |
180 °C | 9.1 % Show Supplier Material materials with Elongation of 9.1 % | dry | ISO 527-1/-2 | |
200 °C | 9.4 % Show Supplier Material materials with Elongation of 9.4 % | dry | ISO 527-1/-2 | |
Flexural modulus | 6 GPa Show Supplier Material materials with Flexural modulus of 6 GPa | conditioned | ISO 178 | |
9 GPa Show Supplier Material materials with Flexural modulus of 9 GPa | dry | ISO 178 | ||
Impact strength, Charpy notched | -30 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m² | dry, conditioned | ISO 179/1eA |
23 °C | 10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m² | dry | ISO 179/1eA | |
23 °C | 18 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 18 kJ/m² | conditioned | ISO 179/1eA | |
Impact strength, Charpy unnotched | -30 °C | 60 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 60 kJ/m² | dry | ISO 179/1eU |
-30 °C | 70 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 70 kJ/m² | conditioned | ISO 179/1eU | |
23 °C | 75 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 75 kJ/m² | dry | ISO 179/1eU | |
23 °C | 100 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | conditioned | ISO 179/1eU | |
Tensile strength | -40 °C | 240 MPa Show Supplier Material materials with Tensile strength of 240 MPa | dry | ISO 527-1/-2 |
115 MPa Show Supplier Material materials with Tensile strength of 115 MPa | conditioned | ISO 527-1/-2 | ||
205 MPa Show Supplier Material materials with Tensile strength of 205 MPa | dry | ISO 527-1/-2 | ||
120 °C | 110 MPa Show Supplier Material materials with Tensile strength of 110 MPa | dry | ISO 527-1/-2 | |
160 °C | 100 MPa Show Supplier Material materials with Tensile strength of 100 MPa | dry | ISO 527-1/-2 | |
180 °C | 95 MPa Show Supplier Material materials with Tensile strength of 95 MPa | dry | ISO 527-1/-2 | |
200 °C | 90 MPa Show Supplier Material materials with Tensile strength of 90 MPa | dry | ISO 527-1/-2 |
Thermal
Property | Value | Condition | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 2.5e-07 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.5e-07 1/K | dry | ISO 11359-1/-2 | Parallel | |
6e-07 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6e-07 1/K | dry | ISO 11359-1/-2 | Normal | ||
Glass transition temperature | 75 °C Show Supplier Material materials with Glass transition temperature of 75 °C | dry | ISO 11357-1/-2 | 10°C/min | |
Heat deflection temperature | 285 °C Show Supplier Material materials with Heat deflection temperature of 285 °C | dry | ISO 75-1/-2 | 2 MPa | |
290 °C Show Supplier Material materials with Heat deflection temperature of 290 °C | dry | ISO 75-1/-2 | 0.45 MPa | ||
Melting point | 295 °C Show Supplier Material materials with Melting point of 295 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Vicat softening temperature | 290 °C Show Supplier Material materials with Vicat softening temperature of 290 °C | dry | ISO 306 | 50°C/h 50N |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Shrinkage | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | dry | Sim. to ISO 294-4 | Parallel |
1.3 % Show Supplier Material materials with Shrinkage of 1.3 % | dry | Sim. to ISO 294-4 | Normal | |
Viscosity number | 145 cm³/gr Show Supplier Material materials with Viscosity number of 145 cm³/gr | dry | ISO 307, 1157, 1628 |
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber |