General
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Density | 1.27 g/cm³ Show Supplier Material materials with Density of 1.27 g/cm³ | dry | ISO 1183 | |
Moisture absorption | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | dry | Sim. to ISO 62 | |
Water absorption | 0.22 % Show Supplier Material materials with Water absorption of 0.22 % | dry | ISO 62 | at 23°C after 24h |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 0.3 GPa Show Supplier Material materials with Elastic modulus of 0.3 GPa | dry | ISO 527-1/-2 | ||
Elongation | 50 % Show Supplier Material materials with Elongation of 50 % | dry | ISO 527-1/-2 | ||
Hardness, Shore A | 98 [-] Show Supplier Material materials with Hardness, Shore A of 98 [-] | dry | ISO 868 | 3s | |
Impact strength, Charpy unnotched | -30 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 5 kJ/m² | dry | ISO 179/1eU | |
Tensile strength | 32 MPa Show Supplier Material materials with Tensile strength of 32 MPa | dry | ISO 527-1/-2 |
Thermal
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Glass transition temperature | -10 °C Show Supplier Material materials with Glass transition temperature of -10 °C | dry | ISO 11357-1/-2 | 10°C/min |
Melting point | 208 °C Show Supplier Material materials with Melting point of 208 °C | dry | ISO 11357-1/-3 | 10°C/min |
Vicat softening temperature | 90 °C Show Supplier Material materials with Vicat softening temperature of 90 °C | dry | ISO 306 | 50°C/h 50N |
Rheological Properties
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Melt volume-flow rate | 230 °C | 9 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 9 cm³/10min | dry | ISO 1133 |
Technological properties
Property |
---|